Mechanical properties of hybrid (medium modulus graphite, Thornel P-55 Kevlar/Epoxy) composites
Journal Article
·
· SAMPE Q.; (United States)
OSTI ID:6715555
This paper treats the mechanical behavior of hybrid (Thornel P-55-Kevlar/Epoxy) composites under ambient conditions and under hostile environments. Interply (core/shell) and intraply tubes (5.75'' I.D.) were filament wound and NOL rings were machined from them. Apparently modulus and apparent strength were measured using the split D (ASTM D2290) test. The influence of boiling water exposure (2 hrs and 24 hrs) on short beam shear strength, apparent modulus, and apparent strength was also evaluated at room temperature and the fracture toughness for above configurations was measured at room temperature. Scanning electron microscopy was used to examine failure modes. 6 references, 4 figures, 3 tables.
- Research Organization:
- B.F. Goodrich R and D Center, Brecksville, OH
- OSTI ID:
- 6715555
- Journal Information:
- SAMPE Q.; (United States), Vol. 18:2
- Country of Publication:
- United States
- Language:
- English
Similar Records
Tensile and fatigue strength properties of Kevlar 29 aramid/epoxy unidirectional composites
Failure analyses of filament-wound graphite/epoxy cylinders under biaxial loading
Engineering properties of a filament-wound Kevlar 49/epoxy composite
Technical Report
·
Wed Jul 22 00:00:00 EDT 1981
·
OSTI ID:6715555
Failure analyses of filament-wound graphite/epoxy cylinders under biaxial loading
Journal Article
·
Tue Oct 01 00:00:00 EDT 1985
· SAMPE Q.; (United States)
·
OSTI ID:6715555
Engineering properties of a filament-wound Kevlar 49/epoxy composite
Journal Article
·
· Compos. Technol. Rev.; (United States)
·
OSTI ID:6715555