The crystalline phases in rapidly solidified Al{sub 65}Cu{sub 20}Fe{sub 15} alloy powders
Journal Article
·
· Scripta Metallurgica et Materialia
- Hunan Univ. (China). Materials Research and Test Center
- Central-South Univ. of Technology, Hunan (China). Powder Metallurgy Research Institute
- Academia Sinica, Shenyang (China). Lab. of Atomic Imaging of Solids
An Al{sub 65}Cu{sub 20}Fe{sub 15} alloy with the composition of Al-65at%, Cu-20at% and Fe-15at% was prepared from 99.5% pure starting materials. Alloy powders were then produced with a rapidly solidified (RS) device developed by Chen et al. The powders obtained have an average particle size of about 15{mu}m and their cooling rates are estimated to be 10{sup 5}--10{sup 7} K/S. The powders were uniformly sprinkled on to microgrids for observation by transmission electron microscope (H-800 transmission electron microscope equipped with an EDAX SW9100 composition analysis system).
- OSTI ID:
- 64352
- Journal Information:
- Scripta Metallurgica et Materialia, Vol. 32, Issue 9; Other Information: PBD: 1 May 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Electron microscopy of rapidly solidified weldments in a powder-metallurgy Al-Fe-Ce alloy
Rapidly solidified powder aluminum alloys; Proceedings of the Symposium, Philadelphia, PA, April 4, 5, 1984
A Comparison of Solidification Structures and Submicroscale Cellular Segregation in Rapidly Solidified Stainless Steels Produced via Two-Piston Splat Quenching and Laser Powder Bed Fusion
Technical Report
·
Sun Jan 01 00:00:00 EST 1989
·
OSTI ID:64352
Rapidly solidified powder aluminum alloys; Proceedings of the Symposium, Philadelphia, PA, April 4, 5, 1984
Conference
·
Wed Jan 01 00:00:00 EST 1986
·
OSTI ID:64352
A Comparison of Solidification Structures and Submicroscale Cellular Segregation in Rapidly Solidified Stainless Steels Produced via Two-Piston Splat Quenching and Laser Powder Bed Fusion
Journal Article
·
Thu Jul 13 00:00:00 EDT 2023
· Microscopy and Microanalysis
·
OSTI ID:64352
+3 more