Adhesion of anodic films on aluminum-lithium alloys
- Univ. of Manchester Institute of Science and Technology (United Kingdom). Corrosion and Protection Centre
- Tohoku Univ., Sendai (Japan). Inst. for Materials Research
- Keio Univ., Hiyoshi, Yokohama (Japan). University Chemical Lab.
During anodizing of certain binary Al alloys, the growing anodic oxide film detaches from the alloy substrate, subsequently allowing access of the electrolyte to the underlying bare metal and re-anodizing at a high current density. An Al-3% Li alloy was shown to reveal these phenomena, which are associated with the development of voids at the alloy/film interface as the film thickens. The development of voids, assisting the film detachment, was attributed to the reduced volume of lithium oxide (Li[sub 2]O) formed at the alloy/film interface and compared to that of alumina (Al[sub 2]O[sub 3]).
- OSTI ID:
- 6388055
- Journal Information:
- Corrosion, Vol. 55:6; ISSN 0010-9312
- Country of Publication:
- United States
- Language:
- English
Similar Records
Porous anodic film formation on an Al-3.5 wt% Cu alloy
The composition and morphology of anodic films on Al-Mo alloys
Development of a Novel Non-Consumable Anode for Electrowinning Primary Aluminum
Journal Article
·
Wed Mar 01 00:00:00 EST 2000
· Journal of the Electrochemical Society
·
OSTI ID:6388055
+3 more
The composition and morphology of anodic films on Al-Mo alloys
Journal Article
·
Sat Mar 01 00:00:00 EST 1997
· Journal of the Electrochemical Society
·
OSTI ID:6388055
+4 more
Development of a Novel Non-Consumable Anode for Electrowinning Primary Aluminum
Technical Report
·
Thu Dec 04 00:00:00 EST 2003
·
OSTI ID:6388055