Stiffness-thermal expansion relationships in high modulus carbon fibers
Improved crystallite orientation in carbon fibers increases the axial stiffness while decreasing the axial coefficient of thermal expansion. Measurements of unidirectional Pitch 120 and Pitch 140 fibers, with axial tensile Young's moduli of 828 GPa and 966 GPa, respectively, in epoxy and aluminum matrices are described. The axial CTE of these fibers was found to be 1.62 + or = 0.04 x 10/sup -6//C in the range of 0 + or 60 C. The positive deviation is attributed to high compressive stresses (P140/Al) of while the most negative value is achievable by fiber misalignments of a few degrees from unidirectional. The stiffness-expansion relation changes for fiber stiffness above 680 GPa. This suggests a decoupling of the coefficient of thermal expansion dependence on preferred orientation, with possible emphasis on defect structure. 29 references.
- Research Organization:
- Aerospace Corp., El Segundo, CA
- OSTI ID:
- 6324046
- Journal Information:
- J. Compos. Mater.; (United States), Vol. 21
- Country of Publication:
- United States
- Language:
- English
Similar Records
Axial and radial coefficients of thermal expansion of carbon fibers in the 20-430 C temperature range as derived from the thermal expansion of 1-D-C-SiO2(B2O3) composites
Study of zero CTE (coefficients of thermal expansion) of graphite/epoxy composites