Title: Iron-niobium-aluminum alloy having high-temperature corrosion resistance

Full Record
Other Related Research

Abstract

An alloy for use in high temperature sulfur and oxygen containing environments, having aluminum for oxygen resistance, niobium for sulfur resistance and the balance iron, is discussed. 4 figs., 2 tabs.

Inventors:: Hsu, Huey S.

Publication Date:: 1988-04-14

Research Org.:: Oak Ridge National Lab., TN (USA)

OSTI Identifier:: 6318397

Patent Number(s):: PATENTS-US-A7181630

Application Number:: ON: DE89009600

Assignee:: Dept. of Energy

DOE Contract Number:: AC05-84OR21400

Resource Type:: Patent

Resource Relation:: Other Information: Portions of this document are illegible in microfiche products

Country of Publication:: United States

Language:: English

Subject:: 36 MATERIALS SCIENCE; ALUMINIUM ALLOYS; CORROSION RESISTANCE; CHROMIUM ALLOYS; IRON BASE ALLOYS; NIOBIUM ALLOYS; COMPARATIVE EVALUATIONS; CORROSION RESISTANT ALLOYS; METALLURGICAL EFFECTS; OXYGEN; SULFUR; ALLOYS; ELEMENTS; IRON ALLOYS; NONMETALS; 360105* - Metals & Alloys- Corrosion & Erosion; 360101 - Metals & Alloys- Preparation & Fabrication

Citation Formats


                    Hsu, Huey S. Iron-niobium-aluminum alloy having high-temperature corrosion resistance.  United States: N. p., 1988. 
        Web.

Copy to clipboard


                    Hsu, Huey S. Iron-niobium-aluminum alloy having high-temperature corrosion resistance.  United States.

Copy to clipboard


                    Hsu, Huey S. Thu .  
        "Iron-niobium-aluminum alloy having high-temperature corrosion resistance".  United States.  https://www.osti.gov/servlets/purl/6318397.

Copy to clipboard


                    
@article{osti_6318397,

  title        = {Iron-niobium-aluminum alloy having high-temperature corrosion resistance},

  author       = {Hsu, Huey S.},

  abstractNote = {An alloy for use in high temperature sulfur and oxygen containing environments, having aluminum for oxygen resistance, niobium for sulfur resistance and the balance iron, is discussed. 4 figs., 2 tabs.},

  doi          = {},

  journal      = {},
number       = ,

  volume       = ,

  place        = {United States},

  year         = {1988},

  month        = {4}

}

Copy to clipboard

Patent:

View Patent (0.50 MB)

Save / Share:

Export Metadata

Save to My Library

Similar records in OSTI.GOV collections:

Iron-aluminum alloys having high room-temperature and method for making same

Patent Sikka, V K ; McKamey, C G

A wrought and annealed iron-aluminum alloy is described consisting essentially of 8 to 9.5% aluminum, an effective amount of chromium sufficient to promote resistance to aqueous corrosion of the alloy, and an alloying constituent selected from the group of elements consisting of an effective amount of molybdenum sufficient to promote solution hardening of the alloy and resistance of the alloy to pitting when exposed to solutions containing chloride, up to about 0.05% carbon with up to about 0.5% of a carbide former which combines with the carbon to form carbides for controlling grain growth at elevated temperatures, and mixtures thereof,more »« less
Iron-aluminum alloys having high room-temperature and method for making same

Patent Sikka, Vinod K ; McKamey, Claudette G

Iron-aluminum alloys having selectable room-temperature ductilities of greater than 20%, high resistance to oxidation and sulfidation, resistant pitting and corrosion in aqueous solutions, and possessing relatively high yield and ultimate tensile strengths are described. These alloys comprise 8 to 9.5% aluminum, up to 7% chromium, up to 4% molybdenum, up to 0.05% carbon, up to 0.5% of a carbide former such as zirconium, up to 0.1 yttrium, and the balance iron. These alloys in wrought form are annealed at a selected temperature in the range of 700.degree. C. to about 1100.degree. C. for providing the alloys with selected room-temperature ductilitiesmore » in the range of 20 to about 29%.« less
Full Text Available
High-temperature corrosion-resistant iron-aluminide (FeAl) alloys exhibiting improved weldability

Patent Maziasz, P J ; Goodwin, G M ; Liu, C T

This invention relates to improved corrosion-resistant iron-aluminide intermetallic alloys. The alloys of this invention comprise, in atomic percent, from about 30% to about 40% aluminum alloyed with from about 0.1% to about 0.5% carbon, no more than about 0.04% boron such that the atomic weight ratio of boron to carbon in the alloy is in the range of from about 0.01:1 to about 0.08:1, from about 0.01 to about 3.5% of one or more transition metals selected from Group IVB, VB, and VIB elements and the balance iron wherein the alloy exhibits improved resistance to hot cracking during welding. 13more » figs.« less
Iron aluminide alloys with improved properties for high temperature applications

Patent McKamey, C G ; Liu, C T

An improved iron aluminide alloy of the DO[sub 3] type is described that has increased room temperature ductility and improved high elevated temperature strength. The alloy system further is resistant to corrosive attack in the environments of advanced energy conversion systems such as those using fossil fuels. The resultant alloy is relatively inexpensive as contrasted to nickel based and high nickel steels currently utilized for structural components. The alloy system consists essentially of 26--30 at. % aluminum, 0.5--10 at. % chromium, 0.02--0.3 at. % boron plus carbon, up to 2 at. % molybdenum, up to 1 at. % niobium, upmore »« less
Oxidation, carburization and/or sulfidation resistant iron aluminide alloy

Patent Sikka, Vinod K. ; Deevi, Seetharama C. ; Fleischhauer, Grier S. ; ...

The invention relates generally to aluminum containing iron-base alloys useful as electrical resistance heating elements. The aluminum containing iron-base alloys have improved room temperature ductility, electrical resistivity, cyclic fatigue resistance, high temperature oxidation resistance, low and high temperature strength, and/or resistance to high temperature sagging. The alloy has an entirely ferritic microstructure which is free of austenite and includes, in weight %, over 4% Al, .ltoreq.1% Cr and either .gtoreq.0.05% Zr or Zro.sub.2 stringers extending perpendicular to an exposed surface of the heating element or .gtoreq.0.1% oxide dispersoid particles. The alloy can contain 14-32% Al, .ltoreq.2% Ti, .ltoreq.2% Mo, .ltoreq.1%more »« less
Full Text Available

Similar Records