Development of Ultrafine, Lamellar Structures in Two-Phase {gamma}-TiAl Alloys
Processing of two-phase gamma-TiAl alloys (Ti-47Al-2Cr-2Nb or minor modifications thereof) above the alpha-transus temperature (T {sub alpha}) produced unique refined-colony/ultrafine lamellar structures in both powder- and ingot-metallurgy (P/M and I/M, respectively) alloys. These ultrafine lamellar structures consist of fine laths of the gamma and alpha {sub 2} phases, with average interlamellar spacings (lambda {sub Lambda}) of 100-200 nm and alpha {sub 2}-alpha {sub 2} spacings (lambda {sub alpha}) of 200-500 nm, and are dominated by gamma/alpha {sub 2} interfaces. This characteristic microstructure forms by extruding P/M Ti-47Al-2Cr-2Nb alloys above T {sub alpha}, and also forms with finer colony size but slightly coarser fully-lamellar structures by hot-extruding similar I/M alloys. Alloying additions of B and W refine lambda {sub L} and lambda {sub alpha} in both I/M Ti-47Al (cast and heat-treated above T {sub alpha}) or in extruded Ti-47Al-2Cr-2Nb alloys. The ultrafine lamellar structure in the P/M alloy remains stable during heat-treatment at 900 {degrees}C for 2h, but becomes unstable after 4h at 982 {degrees}C; the ultrafine lamellar structure remains relatively stable after aging for {gt}5000 h at 800 {degrees}C. Additions of B+W dramatically improve the coarsening resistance of lambda L and lambda alpha in the I/M Ti-47Al alloys aged for 168 h at 1000{degrees}C. In both the P/M and I/M Ti-47Al-2Cr-2Nb alloys, these refined-colony/ultrafine-lamellar structures correlate with high strength and good ductility at room temperature, and very good strength at high temperatures. While refining the colony size improves the room-temperature ductility, alloys with finer lambda {sub L} are stronger at both room- and high-temperatures. Additions of B+W produce finer as-processed lambda {sub L} and lambda {sub alpha} in I/M TiAl alloys, and stabilize such structures during heat-treatment or aging.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Assistant Secretary for Energy Efficiency and Renewable Energy, Washington, DC (United States); USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC05-96OR22464
- OSTI ID:
- 621541
- Report Number(s):
- CONF-970201-33; ON: DE97008429; TRN: AD-A332 03
- Resource Relation:
- Conference: 126. annual meeting of the Minerals, Metals and Materials Society, Orlando, FL (United States), 9-13 Feb 1997; Other Information: DN: Presented at Symposium on Fundamentals of Gamma Titanium Aluminides, 1997TMS Annual Meeting, Orlando, FL.; PBD: 1997
- Country of Publication:
- United States
- Language:
- English
Similar Records
Stability of ultrafine lamellar structures during aging in two-phase {gamma}-TiAl alloys
Ultrafine fully-lamellar structures in two-phase {gamma}-TiAl alloys