Title: Perovskite-type oxides. 1: Structural, magnetic, and morphological properties of LaMn[sub 1[minus]x]Cu[sub x]O[sub 3] and LaCo[sub 1[minus]x]Cu[sub x]O[sub 3] solid solutions with large surface area

Abstract

Perovskite-type compounds of general formula LaMn[sub 1[minus]x]Cu[sub x]O[sub 3] and LaCo[sub 1[minus]x]Cu[sub x]O[sub 3] (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) were prepared by calcining the citrate gel precursors at 823, 923, and 1073 K. The decomposition of the precursors was followed by thermal analysis and the oxides were investigated by means of elemental analysis (atomic absorption and redox titration), X-ray powder diffraction, BET surface area, X-ray absorption (EXAFS and XANES), electron microscopy (SEM and TEM), and magnetic susceptibility. LaMn[sub 1[minus]x]Cu[sub x]O[sub 3] samples are perovskite-like single phases up to x = 0.6. At x = 0.8 CuO and La[sub 2]CuO[sub 4] phases are present in addition to perovskite. Magnetic susceptibility studies show a ferromagnetic behavior that decreases with increase in x. Materials with not very clear morphology and crystals with definite structure are distinguishable by SEM for samples calcined at 1073 and at 1273 K, respectively. TEM patterns, for samples calcined at 1073 K, evidence almost regular hexagonal prismatic crystals connected to form linked structures and some spotty crystals, suggesting short-range ordered local defects. For copper-containing samples, calcined at 1273 K, a higher degree of defectivity (probably associated with the interaction of anion vacancies) and the occurrence ofmore » planar faults are shown by TEM.« less

Authors:
; ; ; ;  [1];  [2];  [3]
  1. (Univ. La Sapienza, Rome (Italy). Dept. di Chimica)
  2. (CNR, Naples (Italy). Ist. di Ricerche Sulla Combustione)
  3. (Univ. Federico II, Naples (Italy). Dept. di Ingegneria Chimica)
Publication Date:
OSTI Identifier:
6108652
Resource Type:
Journal Article
Journal Name:
Journal of Solid State Chemistry
Additional Journal Information:
Journal Volume: 146:2; Journal ID: ISSN 0022-4596
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; COBALT OXIDES; COPPER OXIDES; CRYSTAL STRUCTURE; EXPERIMENTAL DATA; LANTHANUM OXIDES; LATTICE PARAMETERS; MAGNETIC PROPERTIES; MANGANESE OXIDES; MICROSCOPY; PEROVSKITES; SOLID SOLUTIONS; X-RAY DIFFRACTION; CHALCOGENIDES; COBALT COMPOUNDS; COHERENT SCATTERING; COPPER COMPOUNDS; DATA; DIFFRACTION; DISPERSIONS; INFORMATION; LANTHANUM COMPOUNDS; MANGANESE COMPOUNDS; MINERALS; MIXTURES; NUMERICAL DATA; OXIDES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; RARE EARTH COMPOUNDS; SCATTERING; SOLUTIONS; TRANSITION ELEMENT COMPOUNDS; 360202* - Ceramics, Cermets, & Refractories- Structure & Phase Studies; 360204 - Ceramics, Cermets, & Refractories- Physical Properties

Citation Formats

Porta, P., De Rossi, S., Faticanti, M., Minelli, G., Pettiti, I., Lisi, L., and Turco, M. Perovskite-type oxides. 1: Structural, magnetic, and morphological properties of LaMn[sub 1[minus]x]Cu[sub x]O[sub 3] and LaCo[sub 1[minus]x]Cu[sub x]O[sub 3] solid solutions with large surface area. United States: N. p., 1999. Web. doi:10.1006/jssc.1999.8326.
Porta, P., De Rossi, S., Faticanti, M., Minelli, G., Pettiti, I., Lisi, L., & Turco, M. Perovskite-type oxides. 1: Structural, magnetic, and morphological properties of LaMn[sub 1[minus]x]Cu[sub x]O[sub 3] and LaCo[sub 1[minus]x]Cu[sub x]O[sub 3] solid solutions with large surface area. United States. doi:10.1006/jssc.1999.8326.
Porta, P., De Rossi, S., Faticanti, M., Minelli, G., Pettiti, I., Lisi, L., and Turco, M. Wed . "Perovskite-type oxides. 1: Structural, magnetic, and morphological properties of LaMn[sub 1[minus]x]Cu[sub x]O[sub 3] and LaCo[sub 1[minus]x]Cu[sub x]O[sub 3] solid solutions with large surface area". United States. doi:10.1006/jssc.1999.8326.
@article{osti_6108652,
title = {Perovskite-type oxides. 1: Structural, magnetic, and morphological properties of LaMn[sub 1[minus]x]Cu[sub x]O[sub 3] and LaCo[sub 1[minus]x]Cu[sub x]O[sub 3] solid solutions with large surface area},
author = {Porta, P. and De Rossi, S. and Faticanti, M. and Minelli, G. and Pettiti, I. and Lisi, L. and Turco, M.},
abstractNote = {Perovskite-type compounds of general formula LaMn[sub 1[minus]x]Cu[sub x]O[sub 3] and LaCo[sub 1[minus]x]Cu[sub x]O[sub 3] (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) were prepared by calcining the citrate gel precursors at 823, 923, and 1073 K. The decomposition of the precursors was followed by thermal analysis and the oxides were investigated by means of elemental analysis (atomic absorption and redox titration), X-ray powder diffraction, BET surface area, X-ray absorption (EXAFS and XANES), electron microscopy (SEM and TEM), and magnetic susceptibility. LaMn[sub 1[minus]x]Cu[sub x]O[sub 3] samples are perovskite-like single phases up to x = 0.6. At x = 0.8 CuO and La[sub 2]CuO[sub 4] phases are present in addition to perovskite. Magnetic susceptibility studies show a ferromagnetic behavior that decreases with increase in x. Materials with not very clear morphology and crystals with definite structure are distinguishable by SEM for samples calcined at 1073 and at 1273 K, respectively. TEM patterns, for samples calcined at 1073 K, evidence almost regular hexagonal prismatic crystals connected to form linked structures and some spotty crystals, suggesting short-range ordered local defects. For copper-containing samples, calcined at 1273 K, a higher degree of defectivity (probably associated with the interaction of anion vacancies) and the occurrence of planar faults are shown by TEM.},
doi = {10.1006/jssc.1999.8326},
journal = {Journal of Solid State Chemistry},
issn = {0022-4596},
number = ,
volume = 146:2,
place = {United States},
year = {1999},
month = {9}
}