New dual-phase polymer electrolytes prepared from NBR/SBR lattices. [polyacryloNitrile-Butadiene Rubber/poly(Styrene-Butadiene) copolymer Rubber]
- Nippon Telegraph and Telephone Corp., Tokyo (Japan). NTT Interdisciplinary Research Lab.
A new type of Li[sup +] ion conducting polymer electrolytes consisting of two phases, one of which is a highly polar region (impregnated with lithium salt solution), forming ion-conductive channels, while the other is a nonpolar region, forming supporting polymer matrices have been prepared from NBR/SBR lattices. TEM measurement and EDX analysis show evidence that dual-phase structure is constructed in the electrolyte. Ionic conductivity of the electrolyte increases with increase of lithium salt solution content. Maximum ionic conductivity of 2.2 [times] 10[sup [minus]3] S/cm is obtained at the lithium salt solution content of 60.5% (w/w). The electrolyte retains rubber-like film with good mechanical strength despite the presence of the solution.
- OSTI ID:
- 6018950
- Journal Information:
- Journal of the Electrochemical Society; (United States), Vol. 140:10; ISSN 0013-4651
- Country of Publication:
- United States
- Language:
- English
Similar Records
Polymer electrolytes with multiple conductive channels prepared from NBR/SBR latex films impregnated with lithium salt and plasticizer
Fracture morphologies of carbon-black-loaded SBR (styrene-butadiene rubber) subjected to low-cycle, high-stress fatigue. [Styrene-butadiene rubber]
Related Subjects
SOLID ELECTROLYTES
FABRICATION
IONIC CONDUCTIVITY
LATEX
LITHIUM COMPOUNDS
MECHANICAL PROPERTIES
PHASE STUDIES
POLYMERS
ALKALI METAL COMPOUNDS
ELASTOMERS
ELECTRIC CONDUCTIVITY
ELECTRICAL PROPERTIES
ELECTROLYTES
ORGANIC COMPOUNDS
ORGANIC POLYMERS
PHYSICAL PROPERTIES
RUBBERS
250903* - Energy Storage- Batteries- Materials
Components
& Auxiliaries