Superabrasive cubic boron nitride-oxide composites prepared by sol-gel processing
Superabrasive cubic boron nitride (CBN) grains were incorporated in different oxide matrices prepared through sol-gel processing. CBN grains of different particle size from 0.5 to 25 microns were homogeneously dispersed in alumina, alumina-silicate and silica gels. Monolithic composites were achieved upon firing to higher temperatures either by sintering or hot-pressing. Densification of these composites versus temperature was monitored by continuous shrinkage measurements in a dilatometer. The effect of particle size and the volume content of CBN on densification of the gel matrix was investigated. Experimental results were compared with the theories on gel shrinkage and densification of heterogeneous ceramic powders. Reactions at the interface between the CBN particles and the gel matrix and some mechanical properties of the composites were studied.
- Research Organization:
- California Univ., Los Angeles, CA (USA)
- OSTI ID:
- 5940472
- Resource Relation:
- Other Information: Thesis (Ph. D.)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Sol-gel synthesis and characteristics of the rare earth phosphate glasses
[open quotes]Inverse[close quotes] organic-inorganic composite materials. 3. High glass content [open quotes]nonshrinking[close quotes] sol-gel composites via poly(silicic acid esters)
Related Subjects
ALUMINIUM OXIDES
FABRICATION
MECHANICAL PROPERTIES
BORON NITRIDES
SILICATES
SILICON OXIDES
COMPARATIVE EVALUATIONS
COMPOSITE MATERIALS
DISPERSIONS
EXPERIMENTAL DATA
GRAIN DENSITY
HOT PRESSING
PARTICLE SIZE
SINTERING
SOL-GEL PROCESS
ALUMINIUM COMPOUNDS
BORON COMPOUNDS
CHALCOGENIDES
CRYSTAL STRUCTURE
DATA
INFORMATION
MATERIALS
MATERIALS WORKING
MICROSTRUCTURE
NITRIDES
NITROGEN COMPOUNDS
NUMERICAL DATA
OXIDES
OXYGEN COMPOUNDS
PNICTIDES
PRESSING
SILICON COMPOUNDS
SIZE
360601* - Other Materials- Preparation & Manufacture
360603 - Materials- Properties