Workability of the supercooled liquid in the Zr{sub 65}Al{sub 10}Ni{sub 10}Cu{sub 15} bulk metallic glass
- Tohoku Univ., Sendai (Japan). Inst. for Materials Research
The workability of the supercooled liquid in metallic glass has been examined through the extrusion of a Zr{sub 6.5}Al{sub 10}Ni{sub 10}Cu{sub 15} at.% bulk glassy alloy with a wide supercooled liquid region. The metallic glass exhibited superplastic-like deformation behavior at high strain rates, resulting in an excellent workability. The working throughout a wide range of extrusion conditions was compatible with retaining the glass phase and the original strength. The extrusion maps and the expression between extrusion temperature, pressure and ram-speed have been established. Moreover, the features of working such as the Barus effect and the advantage of a small stepwise increase in strain rate have been revealed.
- OSTI ID:
- 585943
- Journal Information:
- Acta Materialia, Vol. 46, Issue 1; Other Information: PBD: 19 Dec 1997
- Country of Publication:
- United States
- Language:
- English
Similar Records
The viscosity of the Zr{sub 46.75}Ti{sub 8.25}Cu{sub 7.5}Ni{sub 10}Be{sub 27.5} bulk metallic glass forming alloy in the supercooled liquid
Viscosity of the supercooled liquid and relaxation at the glass transition of the Zr{sub 46.75}Ti{sub 8.25}Cu{sub 7.5}Ni{sub 10}Be{sub 27.5} bulk metallic glass forming alloy