Phase equilibria in the ternary system titanium-boron-carbon: The sections TiC{sub y}-TiB{sub 2} and B{sub 4}C{sub y}-TiB{sub 2}
Journal Article
·
· Journal of Solid State Chemistry
- Institute of Solid State Chemistry, Ekaterinburg (Russian Federation)
The phase diagram of the ternary Ti-B-C system has been constructed from 300 to 3500 K, especially for the sections TiC{sub y}-TiB{sub 2} and B{sub 4}C{sub y}-TiB{sub 2}. The calculation of the energy parameters describing the phase equilibria with the participation of TiB{sub 2} has been carried out in the subregular solutions approximation. The presence of wide homogeneity regions of carbides, TiC{sub 0.47}-TiC{sub 1.0} and B{sub 4}C{sub 0.45}-B{sub 4}C{sub 1.0}, has been taken into account. Ordering in nonstoichiometric titanium carbide TiC{sub y} at a temperature below 950 K has been calculated by the order parameters functional method.
- OSTI ID:
- 569545
- Journal Information:
- Journal of Solid State Chemistry, Vol. 133, Issue 1; Other Information: PBD: Oct 1997
- Country of Publication:
- United States
- Language:
- English
Similar Records
Combustion synthesis and densification of TiC-TiB{sub 2} and TiC-WC powders
HVOF Thermal Spray TiC/TiB2 Coatings for AUSC Boiler/Turbine Components for Enhanced Corrosion Protection
{tau} phase formation in a TiC + TiB{sub 2} composite bonded with a nickel based binder alloy
Book
·
Tue Aug 01 00:00:00 EDT 1995
·
OSTI ID:569545
HVOF Thermal Spray TiC/TiB2 Coatings for AUSC Boiler/Turbine Components for Enhanced Corrosion Protection
Technical Report
·
Wed Dec 07 00:00:00 EST 2016
·
OSTI ID:569545
{tau} phase formation in a TiC + TiB{sub 2} composite bonded with a nickel based binder alloy
Journal Article
·
Fri May 21 00:00:00 EDT 1999
· Scripta Materialia
·
OSTI ID:569545