Phase equilibrium diagram of the nickel-aluminum-tungsten system in the range 1200-2000/sup 0/C, for the concentration region Ni-Ni/sub 0. 5/Al/sub 0. 5/-W
Journal Article
·
· Dokl. Phys. Chem. (Engl. Transl.); (United States)
OSTI ID:5576025
For the purpose of choosing optimum compositions of nickel alloys with aluminium and tungsten the authors conduct experiments on the phase transformations occurring in both binary and ternary forms of the title alloy under conditions of annealing and cooling and at various quantity ratios of the components. Phase diagrams and thermograms are provided for six different compositions.
- Research Organization:
- A. A. Baikov Institute of Metallurgy, Moscow, USSR
- OSTI ID:
- 5576025
- Journal Information:
- Dokl. Phys. Chem. (Engl. Transl.); (United States), Vol. 288:4-6; Other Information: Translated from Dokl. Akad. Nauk SSSR; 288: No. 4, 935-939(Jun 1986)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Development of directionally solidified eutectic nickel and cobalt alloys. Final report Nov 1974--Nov 1975. [Ni--Cr--W--Al; Ni/sub 3/Al--Mo]
The Phase Equilibria in W-Fe-Co-Ni system alloys. II. Isotherms of the Solidus and the phase composition of Alloys containing 10 and 20% (Fe+Co+Ni) at temperatures above 1200/sup 0/ C
Tungsten--nickel--iron--molybdenum alloys. [1 to 12 percent Ni, 0. 5 to 8 percent Fe, 0. 5 to 25 percent Mo, balance W, other additions]
Technical Report
·
Mon Dec 01 00:00:00 EST 1975
·
OSTI ID:5576025
The Phase Equilibria in W-Fe-Co-Ni system alloys. II. Isotherms of the Solidus and the phase composition of Alloys containing 10 and 20% (Fe+Co+Ni) at temperatures above 1200/sup 0/ C
Journal Article
·
Wed Oct 01 00:00:00 EDT 1986
· Sov. Powder Metall. Met. Ceram. (Engl. Transl.); (United States)
·
OSTI ID:5576025
Tungsten--nickel--iron--molybdenum alloys. [1 to 12 percent Ni, 0. 5 to 8 percent Fe, 0. 5 to 25 percent Mo, balance W, other additions]
Patent
·
Tue Oct 26 00:00:00 EDT 1976
·
OSTI ID:5576025
Related Subjects
36 MATERIALS SCIENCE
ALUMINIUM ALLOYS
PHASE DIAGRAMS
PHASE TRANSFORMATIONS
NICKEL ALLOYS
TUNGSTEN ALLOYS
ANNEALING
BINARY ALLOY SYSTEMS
CHEMICAL COMPOSITION
EQUILIBRIUM
ISOTHERMS
MICROSTRUCTURE
QUANTITY RATIO
TEMPERATURE EFFECTS
TERNARY ALLOY SYSTEMS
VERY HIGH TEMPERATURE
ALLOY SYSTEMS
ALLOYS
CRYSTAL STRUCTURE
DIAGRAMS
HEAT TREATMENTS
360102* - Metals & Alloys- Structure & Phase Studies
ALUMINIUM ALLOYS
PHASE DIAGRAMS
PHASE TRANSFORMATIONS
NICKEL ALLOYS
TUNGSTEN ALLOYS
ANNEALING
BINARY ALLOY SYSTEMS
CHEMICAL COMPOSITION
EQUILIBRIUM
ISOTHERMS
MICROSTRUCTURE
QUANTITY RATIO
TEMPERATURE EFFECTS
TERNARY ALLOY SYSTEMS
VERY HIGH TEMPERATURE
ALLOY SYSTEMS
ALLOYS
CRYSTAL STRUCTURE
DIAGRAMS
HEAT TREATMENTS
360102* - Metals & Alloys- Structure & Phase Studies