Spallation source materials test program
- Los Alamos National Lab., NM (United States). Materials Science and Technology Div.
A spallation source materials program has been developed to irradiate and test candidate materials (Inconel 718, 316L and 304L stainless steel, modified 9Cr-1Mo(T91), Al6061-T6, Al5052-O) for use in the Accelerator Production of Tritium (APT) target and blanket in prototypic proton and neutron fluxes at prototypic temperatures. The study uses the 800 MeV, 1mA proton accelerator at the Los Alamos Neutron Science Center (LANSCE) which produces a Gaussian beam with 2 sigma = 3 cm. The experimental set-up contains prototypic modules of the tungsten neutron source and the lead/aluminum blanket with mechanical testing specimens of candidate APT materials placed in specific locations in the irradiation area. These specimens have been irradiated for greater than 3,600 hours with a maximum proton fluence of 4--5 {times} 10{sup 21} p/cm{sup 2} in the center of the proton beam. Specimens will yield some of the first data on the effect of proton irradiation to high dose on the materials` properties from tensile tests, 3 pt. bend tests, fracture toughness tests, pressurized tubes, U-bend stress corrosion cracking specimens, corrosion measurements and microstructural characterization of transmission electron microscopy specimens.
- Research Organization:
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- W-7405-ENG-36
- OSTI ID:
- 555558
- Report Number(s):
- LA-UR-97-3600; CONF-971125-; ON: DE98001464; TRN: 98:008973
- Resource Relation:
- Conference: 1997 American Nuclear Society (ANS) winter meeting, Albuquerque, NM (United States), 16-20 Nov 1997; Other Information: PBD: [1997]
- Country of Publication:
- United States
- Language:
- English
Similar Records
The Accelerator Production of Tritium Materials Test Program
Fracture Toughness Characterization of 304L and 316L and Alloy 718 After Irradiation in High-Energy, Mixed Proton/Neutron Spectrum