Hydrogen-enhanced fatigue crack growth in Ti-6Al-4V ELI weldments
Journal Article
·
· Metall. Trans.; (United States)
- Research Organization:
- McDonnell Douglas Astronautics Co., Huntington Beach, Calif.
- OSTI ID:
- 5029580
- Journal Information:
- Metall. Trans.; (United States), Vol. 3:1
- Country of Publication:
- United States
- Language:
- English
Similar Records
HYDROGEN-ENHANCED FATIGUE CRACK GROWTH IN Ti--6Al--4V ELI WELDMENTS.
Effect of Test Frequency on Fatigue Crack Growth Rates of Ti-6Al-4V ELI Alloy at Cryogenic Temperature
Fatigue crack growth mechanisms at the microstructure scale in as-fabricated and heat treated Ti-6Al-4V ELI manufactured by electron beam melting (EBM)
Journal Article
·
Sat Jan 01 00:00:00 EST 1972
· Met. Trans. 3: No. 1, 235-43(Jan 1972).
·
OSTI ID:5029580
Effect of Test Frequency on Fatigue Crack Growth Rates of Ti-6Al-4V ELI Alloy at Cryogenic Temperature
Journal Article
·
Fri Mar 31 00:00:00 EST 2006
· AIP Conference Proceedings
·
OSTI ID:5029580
Fatigue crack growth mechanisms at the microstructure scale in as-fabricated and heat treated Ti-6Al-4V ELI manufactured by electron beam melting (EBM)
Journal Article
·
Mon Mar 20 00:00:00 EDT 2017
· Engineering Fracture Mechanics
·
OSTI ID:5029580
+2 more
Related Subjects
08 HYDROGEN
36 MATERIALS SCIENCE
ALUMINIUM ALLOYS
CRACKS
HYDROGEN
METALLURGICAL EFFECTS
TITANIUM BASE ALLOYS
VANADIUM ALLOYS
EMBRITTLEMENT
FATIGUE
WELDED JOINTS
ALLOYS
CRYOGENIC FLUIDS
ELEMENTS
FLUIDS
JOINTS
MECHANICAL PROPERTIES
NONMETALS
TITANIUM ALLOYS
080800* - Hydrogen- Properties & Composition
360105 - Metals & Alloys- Corrosion & Erosion
36 MATERIALS SCIENCE
ALUMINIUM ALLOYS
CRACKS
HYDROGEN
METALLURGICAL EFFECTS
TITANIUM BASE ALLOYS
VANADIUM ALLOYS
EMBRITTLEMENT
FATIGUE
WELDED JOINTS
ALLOYS
CRYOGENIC FLUIDS
ELEMENTS
FLUIDS
JOINTS
MECHANICAL PROPERTIES
NONMETALS
TITANIUM ALLOYS
080800* - Hydrogen- Properties & Composition
360105 - Metals & Alloys- Corrosion & Erosion