Phase Transformation of Zirconium Oxide. Influence of Pressure and Temperature.
Journal Article
·
· Journal of Chemical and Engineering Data
Monoclinic zirconia was pressed to approximates 20,000 atm at >1800 deg C, quenched, fired for 1 hr at 1350 deg C, and quenched. X-ray diffraction patterns were obtained while quenching was repeated through the phase transformation temperature range 800 to 1240 deg C; the results show that the new monoclinic-tetragonal phase transformation is shifted to 950 to 1000 deg C and that the tetragonal phase is stabilized at low temperitures. (D.L.C.)
- Research Organization:
- Wright-Patterson Air Force Base, Ohio
- Sponsoring Organization:
- USDOE
- NSA Number:
- NSA-17-004519
- OSTI ID:
- 4753861
- Journal Information:
- Journal of Chemical and Engineering Data, Vol. 7, Issue 4; Other Information: Orig. Receipt Date: 31-DEC-63; ISSN 0021-9568
- Publisher:
- American Chemical Society
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
THE INFLUENCE OF PRESSURE AND TEMPERATURE ON ZIRCONIUM OXIDE
Preparation and characterization of alumina dispersed in Y-TZP
Thermal stability and phase transformation in fully indium oxide (InO{sub 1.5}) stabilized zirconia
Technical Report
·
Tue Nov 01 00:00:00 EST 1960
·
OSTI ID:4753861
Preparation and characterization of alumina dispersed in Y-TZP
Conference
·
Fri Sep 01 00:00:00 EDT 1995
·
OSTI ID:4753861
Thermal stability and phase transformation in fully indium oxide (InO{sub 1.5}) stabilized zirconia
Journal Article
·
Sun Jan 15 00:00:00 EST 2017
· Materials Characterization
·
OSTI ID:4753861