THE CRYSTAL STRUCTURE OF Pu$sub 3$Co
Technical Report
·
OSTI ID:4752825
A Pu-- Co ingot was prepared by arc melting and heat treated at 440 deg C for one week. It was impossible to obtain good quality crystals due to distortion caused by crushing, but crystals of usable quality were found. Lattice constants and intensities were measured using a single crystal orienter and scintillation counter. Crystallographic data, least-squares parameters, and interatomic distances in Pu/sub 3/Co is presented. (H.G.G.)
- Research Organization:
- Los Alamos Scientific Lab., N. Mex.
- DOE Contract Number:
- W-7405-ENG-36
- NSA Number:
- NSA-17-016647
- OSTI ID:
- 4752825
- Report Number(s):
- LADC-5363
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-63
- Country of Publication:
- United States
- Language:
- English
Similar Records
CERAMICS RESEARCH
The complex metal-rich boride Ti{sub 1+x}Rh{sub 2-x+y}Ir{sub 3-y}B{sub 3} (x=0.68, y=1.06) with a new structure type containing B{sub 4} zigzag fragments: Synthesis, crystal chemistry and theoretical calculations
Synthesize and microstructure characterization of Ni{sub 43}Mn{sub 41}Co{sub 5}Sn{sub 11} Heusler alloy
Technical Report
·
Thu Oct 31 00:00:00 EST 1963
·
OSTI ID:4752825
The complex metal-rich boride Ti{sub 1+x}Rh{sub 2-x+y}Ir{sub 3-y}B{sub 3} (x=0.68, y=1.06) with a new structure type containing B{sub 4} zigzag fragments: Synthesis, crystal chemistry and theoretical calculations
Journal Article
·
Wed Aug 15 00:00:00 EDT 2012
· Journal of Solid State Chemistry
·
OSTI ID:4752825
Synthesize and microstructure characterization of Ni{sub 43}Mn{sub 41}Co{sub 5}Sn{sub 11} Heusler alloy
Journal Article
·
Fri Jun 17 00:00:00 EDT 2016
· AIP Conference Proceedings
·
OSTI ID:4752825