CORROSION AND ELECTROCHEMICAL PROPERTIES OF TITANIUM, ZIRCONIUM AND TITANIUM-ZIRCONIUM ALLOYS IN ACID SOLUTIONS. PART II
Journal Article
·
· J. Appl. Chem. (London)
OSTI ID:4735511
The corrosion and electrochemical behavior of titanium, zirconium, and titanium --zirconium alloys in solutions of sulfuric, nitric, and phosphoric acids and also in mixtures of nitric and phosphoric acids, were investigated. Alloying titanium with zirconium increases the titanium corrosionresistance in sulfuric acid solutions at 100 deg when the concentration of the latter is 80%. At concentrations higher than that neither of the metals nor titanium- zirconium alloys are stable. In phosphoric and nitric acid solutions, titanium-- zirconium alloys have no advantage over titanium and zirconium. (auth)
- Research Organization:
- Inst. of Physical Chemistry, Moscow
- NSA Number:
- NSA-17-008747
- OSTI ID:
- 4735511
- Journal Information:
- J. Appl. Chem. (London), Vol. Vol: 12; Other Information: Orig. Receipt Date: 31-DEC-63
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
CORROSION AND ELECTROCHEMICAL BEHAVIOR OF Zr, Ti AND Zr-Ti ALLOYS IN PHOSPHORIC AND NITRIC ACIDS
STUDIES ON THE MECHANISM OF THE ELECTROCHEMICAL CORROSION OF TITANIUM. III. THE CORROSION AND ELECTROCHEMICAL BEHAVIOR OF TITANIUM AND OF ITS PLATINUM AND PALLADIUM ALLOYS IN SULFURIC AND HYDROCHLORIC ACID SOLUTIONS
IN-PILE RADIATION CORROSION EXPERIMENTS WITH ZIRCONIUM, TITANIUM, AND STEEL ALLOYS IN 0.17 m UO$sub 2$SO$sub 4$ SOLUTIONS AT 280 C
Journal Article
·
Wed Aug 01 00:00:00 EDT 1962
· Zh. Prikl. Khim.
·
OSTI ID:4735511
STUDIES ON THE MECHANISM OF THE ELECTROCHEMICAL CORROSION OF TITANIUM. III. THE CORROSION AND ELECTROCHEMICAL BEHAVIOR OF TITANIUM AND OF ITS PLATINUM AND PALLADIUM ALLOYS IN SULFURIC AND HYDROCHLORIC ACID SOLUTIONS
Journal Article
·
Mon May 01 00:00:00 EDT 1961
· Zhur. Fiz. Khim.
·
OSTI ID:4735511
IN-PILE RADIATION CORROSION EXPERIMENTS WITH ZIRCONIUM, TITANIUM, AND STEEL ALLOYS IN 0.17 m UO$sub 2$SO$sub 4$ SOLUTIONS AT 280 C
Technical Report
·
Wed Jul 10 00:00:00 EDT 1963
·
OSTI ID:4735511