Palladium(II)-catalyzed isospecific alternating copolymerization of aliphatic {alpha}-olefins with carbon monoxide and isospecific alternating isomerization cooligomerization of a 1,2-disubstituted olefin with carbon monoxide. Synthesis of novel, optically active, isotatic 1,4- and 1,5-polyketones
- Pennsylvania State Univ., University Park, PA (United States)
The compound [Pd(Me-DUPHOS)(MeCN){sub 2}](BF{sub 4}){sub 2}, 1 [Me-DUPHOS = 1,2-bis(2,5-dimethylphospholano)-benzene], has been found to be an effective catalyst for the highly enantioselective, alternating copolymerization of aliphatic {alpha}-olefins with carbon monoxide to form optically active, isotactic polymers. The {alpha}-olefin--carbon monoxide copolymers, as synthesized in CH{sub 3}NO{sub 2}/CH{sub 3}OH, had a mixture of 1,4-ketone and spiroketal repeating units in the backbone. The interchange between 1,4-keto and spiroketal units was observed even in the absence of any added metal catalyst. The temperature dependence of the molar optical rotation of the isotactic pure poly(1,4-ketone)s indicated that the chirality of the copolymers was due to the presence of stereogenic tertiary carbons in the polymer backbone rather than due to polymer conformation. The degree of enantioselectivity in the formation of chiral, isotactic propylene-carbon monoxide copolymer was found to be > 90{degree} (as determined by NMR spectroscopy using a chiral NMR shift reagent). The isotactic {alpha}-olefin-carbon monoxide copolymers serve as excellent starting materials for the synthesis of other classes of chiral polymers. 14 refs., 10 figs., 1 tab.
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- FG02-84ER13295
- OSTI ID:
- 45025
- Journal Information:
- Journal of the American Chemical Society, Vol. 117, Issue 16; Other Information: PBD: 26 Apr 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Substantially isotactic, linear, alternating copolymers of carbon monoxide and an olefin
Chiral and steric recognition in optically active, isotactic, alternating {alpha}-olefin-carbon monoxide copolymers. Effect on physical properties and chemical reactivity