EMBRITTLEMENT OF NEUTRON-IRRADIATED 20Cr--25Ni--Nb AUSTENITIC STEEL AT 650 DEG C.
Journal Article
·
· J. Iron Steel Inst. (London), 205: 58-61(Jan. 1967).
OSTI ID:4471905
- Research Organization:
- Aktiebolaget Atomenergi, Studsvik, Sweden
- NSA Number:
- NSA-21-011267
- OSTI ID:
- 4471905
- Journal Information:
- J. Iron Steel Inst. (London), 205: 58-61(Jan. 1967)., Other Information: Orig. Receipt Date: 31-DEC-67
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
EMBRITTLEMENT OF NEUTRON-IRRADIATED 20Cr--25Ni--Nb AUSTENITIC STEEL AT 650$sup 0$C.
THE STRUCTURE OF 20Cr-25Ni-Nb STEEL AFTER AGEING FOR UP TO 2000 HOURS IN THE TEMPERATURE RANGE 600-800 DEG C
Radiation response of a Fe–20Cr–25Ni austenitic stainless steel under Fe2+ irradiation at 500 °C
Journal Article
·
Sun Jan 01 00:00:00 EST 1967
· J. Iron Steel Inst. (London), 205: 58-61(Jan. 1967).
·
OSTI ID:4471905
THE STRUCTURE OF 20Cr-25Ni-Nb STEEL AFTER AGEING FOR UP TO 2000 HOURS IN THE TEMPERATURE RANGE 600-800 DEG C
Technical Report
·
Sat Jan 01 00:00:00 EST 1966
·
OSTI ID:4471905
+1 more
Radiation response of a Fe–20Cr–25Ni austenitic stainless steel under Fe2+ irradiation at 500 °C
Journal Article
·
Fri Nov 22 00:00:00 EST 2019
· Materialia
·
OSTI ID:4471905
+5 more