Dislocation pinning in electron-irradiated copper as a function of electron energy and irradiation
Book
·
OSTI ID:4400237
Dislocation priming measurements were performed in the kHz range in ASARCO copper. The samples and irradiation facilities are constructed so as to allow successive irradiation of samples both with electrons and gamma rays. The gamma rays were produced by stopping 2.8-MeV electrons in a gold target. The change of the type of irradiation could be achieved without any handling of the sample. Thus it is possible to detect rather small differences between the two types of irradiation. Recovery experiments at 400 deg K after 75 deg K irradiation and pinning rates during irradiation at 400 deg K and 75 deg K were made. (GE)
- Research Organization:
- Kernforschungsanlage, Juelich, Ger.
- NSA Number:
- NSA-29-010752
- OSTI ID:
- 4400237
- Resource Relation:
- Conference: 5. international conference on internal friction and ultrasonic attenuation in crystalline solids, Aachen, Germany, 27 Aug 1973; Other Information: Orig. Receipt Date: 30-JUN-74; Bib. Info. Source: GE (GE)
- Country of Publication:
- Germany
- Language:
- English
Similar Records
Relation between Hasiguti peaks and pinning stages in cold-worked and electron-irradiated copper
IRRADIATION PINNING AND THERMAL DEPINNING OF DISLOCATIONS
SOLID STATE DIVISION ANNUAL PROGRESS REPORT FOR PERIOD ENDING AUGUST 31, 1959
Book
·
Mon Jan 01 00:00:00 EST 1973
·
OSTI ID:4400237
IRRADIATION PINNING AND THERMAL DEPINNING OF DISLOCATIONS
Journal Article
·
Sun Apr 01 00:00:00 EST 1962
· Acta Met.
·
OSTI ID:4400237
SOLID STATE DIVISION ANNUAL PROGRESS REPORT FOR PERIOD ENDING AUGUST 31, 1959
Technical Report
·
Fri Dec 11 00:00:00 EST 1959
·
OSTI ID:4400237