INFLUENCE OF CHEMICAL COMPOSITION ON RUPTURE TEST PROPERTIES AT 1500 F OF FORGED CHROMIUM-COBALT-NICKEL-IRON BASE ALLOYS
Technical Report
·
OSTI ID:4381480
- Research Organization:
- Michigan Univ.
- NSA Number:
- NSA-06-005381
- OSTI ID:
- 4381480
- Report Number(s):
- NACA-TN-2745
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-52
- Country of Publication:
- United States
- Language:
- English
Similar Records
THE INFLUENCE OF COMPOSITION UPON THE 1500 F CREEP-RUPTURE STRENGTH AND MICROSTRUCTURE OF MOLYBDENUM-CHROMIUM-IRON-NICKEL BASE ALLOYS
INFLUENCE OF CERTAIN COMPOSITION AND FABRICATION VARIABLES ON THE STRESS- RUPTURE PROPERTIES OF A COBALT-BASE ALLOY CONSOLIDATED BY POWDER METALLURGY
RESULTS OF STATIC CORROSION TESTS ON VARIOUS NICKEL-BASE BRAZING ALLOYS USED TO FABRICATE 304 STAINLESS STEEL T-JOINTS. JOINTS TESTED IN SODIUM AND FLUORIDE #44 (NaF-ZrF*SUB 4/-UF*SUB 4/) FOR 100 HOURS AT 1500 F
Technical Report
·
Tue Jul 01 00:00:00 EDT 1958
·
OSTI ID:4381480
INFLUENCE OF CERTAIN COMPOSITION AND FABRICATION VARIABLES ON THE STRESS- RUPTURE PROPERTIES OF A COBALT-BASE ALLOY CONSOLIDATED BY POWDER METALLURGY
Technical Report
·
Wed Aug 01 00:00:00 EDT 1962
·
OSTI ID:4381480
RESULTS OF STATIC CORROSION TESTS ON VARIOUS NICKEL-BASE BRAZING ALLOYS USED TO FABRICATE 304 STAINLESS STEEL T-JOINTS. JOINTS TESTED IN SODIUM AND FLUORIDE #44 (NaF-ZrF*SUB 4/-UF*SUB 4/) FOR 100 HOURS AT 1500 F
Technical Report
·
Wed Dec 01 00:00:00 EST 1954
·
OSTI ID:4381480