A METHOD FOR ROLLING URANIUM FOIL
Technical Report
·
OSTI ID:4355825
Uranium-buttons may be rolled in a simple process by breaking and firing, plating, annealing at 600 deg C for 1/2 hr in a low pressure vacuum furnace, rolling immediately while still hot and then annealing. If cross rolling is done, the piece can be given two passes 90 deg to each other at the same reduction without being annealed between passes. If a 10 to 20% reduction is wanted on every 90 deg turn, the piece should be annealed between each pass. Four passes at 5% with 200 deg heat treatmert between each pass is not as good as one 20% reduction pass. (F.S.)
- Research Organization:
- Los Alamos Scientific Lab., N. Mex.
- NSA Number:
- NSA-12-000913
- OSTI ID:
- 4355825
- Report Number(s):
- LAMS-626
- Resource Relation:
- Other Information: Decl. Mar. 18, 1957. Orig. Receipt Date: 31-DEC-58
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
DEVELOPMENT OF TECHNIQUES FOR ROLLING URANIUM METAL
RECRYSTALLIZATION DIAGRAM OF VANADIUM
RECRYSTALLIZATION OF HEAVILY COLD-ROLLED URANIUM SHEET
Technical Report
·
Wed Nov 15 00:00:00 EST 1950
·
OSTI ID:4355825
+6 more
RECRYSTALLIZATION DIAGRAM OF VANADIUM
Journal Article
·
Sat Jul 21 00:00:00 EDT 1962
· Doklady Akad. Nauk S.S.S.R.
·
OSTI ID:4355825
RECRYSTALLIZATION OF HEAVILY COLD-ROLLED URANIUM SHEET
Technical Report
·
Fri May 01 00:00:00 EDT 1959
·
OSTI ID:4355825