MANUFACTURING METHODS AND PILOT PRODUCTION OF TITANIUM ALLOY CASTINGS AND REPORTS. Interim Engineering Report No. 1. Phase II: Experimental, September 4 to December 4, 1956
Technical Report
·
OSTI ID:4349629
ABSTRACTS A total of nine 6 lb heats of pure Ti were poured from a 9-in. diameter tllt pour skull arc furnace into machined graphite molds in an attempt to obtain gas free castings. Pumping in the pressure range below 10 mu while molten and during freezing and subsequent remelting, as well as heating the mold, did not eliminate gas porosity. The vacuum operation of permanent W electrodes was shown to be possible although somewhat difficult. It is suggested that mold reaction or mold gas desorption is a major source of gas porosity. It is recommended that further studies continue to pursue the elimination of gas porositywith major emphasis put on mold material. (auth)
- Research Organization:
- National Research Corp., Cambridge, Mass.
- DOE Contract Number:
- AF33(600)-32801
- NSA Number:
- NSA-12-001390
- OSTI ID:
- 4349629
- Report Number(s):
- AD-119840
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-58
- Country of Publication:
- United States
- Language:
- English
Similar Records
BERYLLIUM CASTING--PHASE II. Interim Technical Engineering Report No. 5 for Period September 20 to December 19, 1959
BERYLLIUM CASTING. Interim Technical Engineering Report No. 10, Reporting Period, July 5, 1961 to November 4, 1961
BERYLLIUM CASTING--PHASE II. Interim Technical Report No. 6 for December 19, 1959-March 18, 1960
Technical Report
·
Mon Oct 31 00:00:00 EST 1960
·
OSTI ID:4349629
BERYLLIUM CASTING. Interim Technical Engineering Report No. 10, Reporting Period, July 5, 1961 to November 4, 1961
Technical Report
·
Wed Oct 31 00:00:00 EST 1962
·
OSTI ID:4349629
BERYLLIUM CASTING--PHASE II. Interim Technical Report No. 6 for December 19, 1959-March 18, 1960
Technical Report
·
Mon Oct 31 00:00:00 EST 1960
·
OSTI ID:4349629