NEW HIGH TEMPERATURE INTERMETALLIC MATERIALS. Period covered September 2, 1955 through November 2, 1956
Technical Report
·
OSTI ID:4345501
Six ternary systems were investigated as to physical properties, oxidation resistance, mechanical properties, phase studies, and electrical resistivity. They were: Cu, Cr, and Ti with Mo--Si, Cr--Ti--Si, Ti--Al--Ni, and Cr-Ti--Cu. (T.R.H.)
- Research Organization:
- Firth Sterling Inc. American Electro Metal Div., Yonkers, N.Y.
- DOE Contract Number:
- AF33(616)-3198
- NSA Number:
- NSA-12-003696
- OSTI ID:
- 4345501
- Report Number(s):
- WADC-TR-53-190(Pt. 5); AD-1106
- Resource Relation:
- Other Information: Project title: CERAMIC AND CERMET MATERIALS. Task title: HIGH TEMPERATURE AND HIGH STRESS CHARACTERISTICS OF CERAMICS AND CERMETS. Orig. Receipt Date: 31-DEC-58
- Country of Publication:
- United States
- Language:
- English
Similar Records
DEVELOPMENT AND EVALUATION OF HIGH-TEMPERATURE TUNGSTEN ALLOYS. Period covered: May 1, 1957 to September 30, 1958
RESEARCH ON INTERMETALLIC CONTAINERS FOR MELTING TITANIUM. Period covered September 1, 1955 through October 31, 1956
THE PRINCIPLES OF DISPERSION HARDENING WHICH PROMOTE HIGH-TEMPERATURE STRENGTH IN IRON-BASE ALLOYS. Period covered: January 14, 1956 to January 13, 1957
Technical Report
·
Wed Apr 01 00:00:00 EST 1959
·
OSTI ID:4345501
RESEARCH ON INTERMETALLIC CONTAINERS FOR MELTING TITANIUM. Period covered September 1, 1955 through October 31, 1956
Technical Report
·
Mon Oct 01 00:00:00 EDT 1956
·
OSTI ID:4345501
THE PRINCIPLES OF DISPERSION HARDENING WHICH PROMOTE HIGH-TEMPERATURE STRENGTH IN IRON-BASE ALLOYS. Period covered: January 14, 1956 to January 13, 1957
Technical Report
·
Thu Aug 22 00:00:00 EDT 1957
·
OSTI ID:4345501