The stability of vanadium and of the alloy V-3Ti-15Nb in liquid lithium at 700$sup 0$C (in German)
Journal Article
·
· J. Nucl. Mater., v. 51, no. 2, pp. 221-226
OSTI ID:4291272
- Research Organization:
- Kernforschungszentrum Karlsruhe (F.R. Germany). Inst. fuer Material- und Festkoerperforschung
- NSA Number:
- NSA-30-029951
- OSTI ID:
- 4291272
- Journal Information:
- J. Nucl. Mater., v. 51, no. 2, pp. 221-226, Other Information: Orig. Receipt Date: 31-DEC-74; Bib. Info. Source: NL (Netherlands (sent to DOE from))
- Country of Publication:
- Netherlands
- Language:
- German
Similar Records
PLASTIC DEFORMATION OF A NICKEL--CHROMIUM--NIOBIUM ALLOY QUENCHED IN WATER FROM 1200$sup 0$C TO 20$sup 0$C, THEN TEMPERED AT 700$sup 0$C.
Biaxial Thermal Creep of Two Heats of V4Cr4Ti at 700 and 800 C in a Liquid Lithium Environment
NUCLEATION MECHANISM IN A Ni--Cr--Nb--Co ALLOY AT 1150$sup 0$C QUENCHED IN WATER AT 20$sup 0$C AND TEMPERED AT 700--C
Journal Article
·
Thu Jan 01 00:00:00 EST 1970
· Compt. Rend., Ser. C 270: 1273-5(13 Apr 1970).
·
OSTI ID:4291272
Biaxial Thermal Creep of Two Heats of V4Cr4Ti at 700 and 800 C in a Liquid Lithium Environment
Journal Article
·
Mon Jan 01 00:00:00 EST 2007
· Journal of Nuclear Materials
·
OSTI ID:4291272
+6 more
NUCLEATION MECHANISM IN A Ni--Cr--Nb--Co ALLOY AT 1150$sup 0$C QUENCHED IN WATER AT 20$sup 0$C AND TEMPERED AT 700--C
Journal Article
·
Fri Jan 01 00:00:00 EST 1971
· Compt. Rend., Ser. C 273: No. 22, 1497-9 (29 Nov 1971).
·
OSTI ID:4291272
Related Subjects
N50210* -Metals
Ceramics
& Other Materials-Metals & Alloys-Corrosion & Erosion & Surface Phenomena
*LITHIUM- CORROSIVE EFFECTS
*VANADIUM ALLOYS- REDUCTION
*VANADIUM- - REDUCTION
CARBONIZATION
CRYSTAL DEFECTS
GRAIN BOUNDARIES
HIGH TEMPERATURE
LIQUID METALS
NIOBIUM ALLOYS
STABILITY
TITANIUM ALLOYS
Ceramics
& Other Materials-Metals & Alloys-Corrosion & Erosion & Surface Phenomena
*LITHIUM- CORROSIVE EFFECTS
*VANADIUM ALLOYS- REDUCTION
*VANADIUM- - REDUCTION
CARBONIZATION
CRYSTAL DEFECTS
GRAIN BOUNDARIES
HIGH TEMPERATURE
LIQUID METALS
NIOBIUM ALLOYS
STABILITY
TITANIUM ALLOYS