RESULTS OF STATIC CORROSION TESTS ON VARIOUS NICKEL-BASE BRAZING ALLOYS USED TO FABRICATE 304 STAINLESS STEEL T-JOINTS. JOINTS TESTED IN SODIUM AND FLUORIDE #44 (NaF-ZrF*SUB 4/-UF*SUB 4/) FOR 100 HOURS AT 1500 F
Technical Report
·
OSTI ID:4227537
The results of corrosion tests on nickel-base brazing alloys indicated that all the alloys tested had good resistance to attack by fused chloride. The chromium-nickel--phosphorus system showed good resistance to attack by both fused fluoride and sodium. (J.E.D.)
- Research Organization:
- Oak Ridge National Lab., Tenn.
- DOE Contract Number:
- W-7405-ENG-26
- NSA Number:
- NSA-13-022387
- OSTI ID:
- 4227537
- Report Number(s):
- CF-54-12-26
- Resource Relation:
- Other Information: Decl. June 8, 1959. 3p. Orig. Receipt Date: 31-DEC-59
- Country of Publication:
- United States
- Language:
- English
Similar Records
RARE EARTH AND YTTRIUM FLUORIDES. SOLUBILITY RELATIONS IN VARIOUS MOLTEN NaF-ZrF$sub 4$ AND NaF-ZrF$sub 4$-UF$sub 4$ SOLVENTS
Solubility of Noble Gases in Molten Fluorides. I. In Mixtures of NaF–ZrF 4 (53–47 Mole %) and NaF–ZrF 4 –UF 4 (50–46–4 Mole %)
CORROSION RESISTANCE OF NICKEL-BASE ALLOYS IN A NaF-LiF-BeF$sub 2$-ZrF$sub 4$ SALT MIXTURE UNDER HYDROFLUORINATOR CONDITIONS WITH ZIRCALOY-2 DISSOLVING AT 500 C
Journal Article
·
Fri Apr 01 00:00:00 EST 1960
· Journal of Chemical and Engineering Data (U.S.)
·
OSTI ID:4227537
+1 more
Solubility of Noble Gases in Molten Fluorides. I. In Mixtures of NaF–ZrF 4 (53–47 Mole %) and NaF–ZrF 4 –UF 4 (50–46–4 Mole %)
Journal Article
·
Tue Jul 01 00:00:00 EDT 1958
· Journal of Physical Chemistry
·
OSTI ID:4227537
CORROSION RESISTANCE OF NICKEL-BASE ALLOYS IN A NaF-LiF-BeF$sub 2$-ZrF$sub 4$ SALT MIXTURE UNDER HYDROFLUORINATOR CONDITIONS WITH ZIRCALOY-2 DISSOLVING AT 500 C
Technical Report
·
Thu Apr 25 00:00:00 EST 1963
·
OSTI ID:4227537
+1 more