METALLURGICAL INVESTIGATION OF THE STRESS CORROSION FAILURE IN THE STAINLESS STEEL CLAD OF THE S1C REACTOR VESSEL
Technical Report
·
OSTI ID:4184387
- Research Organization:
- Combustion Engineering, Inc. Nuclear Div., Windsor, Conn.
- NSA Number:
- NSA-14-020552
- OSTI ID:
- 4184387
- Report Number(s):
- CEND-78
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-60
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
METALLURGICAL INVESTIGATIONS ON THE CLADDING FAILURE IN THE JPDR PRESSURE VESSEL. II. A STUDY ON THE PITTING CORROSION IN HIGH TEMPERATURE WATER OF A LOW ALLOY STEEL WITHIN THE SIMULATED CRACKS IN THE PROTECTIVE WELD OVERLAY.
METALLURGICAL INVESTIGATIONS ON THE CLADDING FAILURE IN THE JPDR PRESSURE VESSEL. IV. THE EFFECT OF FREQUENCY OF LOADING ON THE FATIGUE OF LOW ALLOY STEEL IN RECIRCULATING DEIONIZED WATER ENVIRONMENT.
METALLURGICAL INVESTIGATIONS ON THE CLADDING FAILURE IN THE JPDR PRESSURE VESSEL. III. EFFECT OF TEMPERATURE ON THE FATIGUE CRACK PROPAGATION IN A LOW ALLOY STEEL IN DEIONIZED WATER.
Technical Report
·
Thu Jan 01 00:00:00 EST 1970
·
OSTI ID:4184387
+1 more
METALLURGICAL INVESTIGATIONS ON THE CLADDING FAILURE IN THE JPDR PRESSURE VESSEL. IV. THE EFFECT OF FREQUENCY OF LOADING ON THE FATIGUE OF LOW ALLOY STEEL IN RECIRCULATING DEIONIZED WATER ENVIRONMENT.
Technical Report
·
Thu Jan 01 00:00:00 EST 1970
·
OSTI ID:4184387
METALLURGICAL INVESTIGATIONS ON THE CLADDING FAILURE IN THE JPDR PRESSURE VESSEL. III. EFFECT OF TEMPERATURE ON THE FATIGUE CRACK PROPAGATION IN A LOW ALLOY STEEL IN DEIONIZED WATER.
Technical Report
·
Thu Jan 01 00:00:00 EST 1970
·
OSTI ID:4184387