Grain boundary migration induced segregation in V-Cr-Ti alloys
- Pacific Northwest National Lab., Richland, WA (United States)
- Univ. of Hokkaido (Japan)
Analytical electron microscopy results are reported for a series of vanadium alloys irradiated in the HFIR JP23 experiment at 500{degrees}C. Alloys were V-5Cr-5Ti and pure vanadium which are expected to have transmuted to V-15Cr-5Ti and V-10Cr following irradiation. Analytical microscopy confirmed the expected transmutation occurred and showed redistribution of Cr and Ti resulting from grain boundary migration in V-5Cr-5Ti, but in pure V, segregation was reduced and no clear trends as a function of position near a boundary were identified.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- DOE Contract Number:
- AC06-76RL01830
- OSTI ID:
- 414859
- Report Number(s):
- DOE/ER-0313/20; ON: DE97000700; TRN: 97:001378
- Resource Relation:
- Other Information: PBD: Oct 1996; Related Information: Is Part Of Fusion materials semiannual progress report for the period ending June 30, 1996; PB: 358 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Tensile properties of V-(4-15)Cr-5Ti alloys irradiated at 400{degrees}C in the HFIR
Revised ANL-reported tensile data for unirradiated and irradiated (FFTF, HFIR) V-Ti and V-Cr-Ti alloys
Effect of heat treatment on grain boundary chemistry and fracture properties of a V-5Cr-5Ti alloy
Technical Report
·
Tue Oct 01 00:00:00 EDT 1996
·
OSTI ID:414859
Revised ANL-reported tensile data for unirradiated and irradiated (FFTF, HFIR) V-Ti and V-Cr-Ti alloys
Technical Report
·
Sun Mar 01 00:00:00 EST 1998
·
OSTI ID:414859
Effect of heat treatment on grain boundary chemistry and fracture properties of a V-5Cr-5Ti alloy
Journal Article
·
Sun Oct 01 00:00:00 EDT 1995
· Scripta Metallurgica et Materialia
·
OSTI ID:414859