HIGH TEMPERATURE OXIDATION OF IRON-CHROMIUM BINARY ALLOYS IN WATER VAPOR. PART 1. A PRELIMINARY STUDY OF TEH MECHANISM OF OXIDATION OF IRON-CHROMIUM BINARY ALLOYS IN WATER VAPOR
Technical Report
·
OSTI ID:4112739
The oxidation of Cr-Fe alloys (Cr content of 5, 10, 15, 20, and 25 wt.%) in a water vapor-argon atmosphere was studied at 700, 900, and llOO/sup o/C. A mechanism for the oxidation process is suggested in the form of wustite decomposition at the outer-inner scale layer boundary, giving rise to Fe/sup 2+/ diffusion to the outer layer and O/sup 2/diffusion to the alloy-oxide interface. (C.J.G.)
- Research Organization:
- Naval Research Lab., Washington, D.C.
- NSA Number:
- NSA-15-003032
- OSTI ID:
- 4112739
- Report Number(s):
- NRL-5506
- Resource Relation:
- Other Information: Project RR-007-01-42-5406. Orig. Receipt Date: 31-DEC-61
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
Thermal healing of defects in oxide scales on iron-chromium alloys
KINETICS OF OXIDATION OF IRON-CHROMIUM ALLOYS AND THE TRANSPORT PROPERTIES OF THE OXIDES IN CARBON DIOXIDE-CARBON MONOXIDE MIXTURES. End of Year Report
New Creep-Resistant Cast Alloys with Improved Oxidation Resistance in Water Vapor at 650–800°C
Technical Report
·
Sun Apr 01 00:00:00 EST 1990
·
OSTI ID:4112739
KINETICS OF OXIDATION OF IRON-CHROMIUM ALLOYS AND THE TRANSPORT PROPERTIES OF THE OXIDES IN CARBON DIOXIDE-CARBON MONOXIDE MIXTURES. End of Year Report
Technical Report
·
Thu Jan 31 00:00:00 EST 1963
·
OSTI ID:4112739
New Creep-Resistant Cast Alloys with Improved Oxidation Resistance in Water Vapor at 650–800°C
Journal Article
·
Thu Aug 13 00:00:00 EDT 2015
· Frontiers in Materials
·
OSTI ID:4112739