IRRADIATION OF WROUGHT URANIUM PLATE
Technical Report
·
OSTI ID:4072060
Wrought uranium plate, clad in 1100 aluminum with a nickel bonding layer, was irradiated to a maximum exposure of 1600 Mwd/T in the Materials Testing Reactor and was found to be suitable as a fuel-element material. Retatransformed plate, or beta-transformed plate thst was cold stretched 2.25%, did not change appreciably in dimensions but roughened on the surface. As-roaled plate increased in length, but did not roughen. Irradiation reduced the strength and virtually eliminsted the ductility of the plate. Abrasion of the cladding caused corrosion pitting. The strength of the nickel difusion bond between core and cladding was unimpsired by the irradiation. (auth)
- Research Organization:
- Du Pont de Nemours (E.I.) & Co. Savannah River Lab., Aiken, S.C.
- DOE Contract Number:
- AT(07-2)-1
- NSA Number:
- NSA-15-011702
- OSTI ID:
- 4072060
- Report Number(s):
- DP-211
- Resource Relation:
- Other Information: Decl. Oct. 12, 1960. Orig. Receipt Date: 31-DEC-61
- Country of Publication:
- United States
- Language:
- English
Similar Records
IRRADIATION OF POWDER METALLURGY PLATES
FUEL BEARING FIBERGLAS IN ALUMINUM-BASE FUEL ELEMENTS. Final Report
THE APPLICATION OF A NOMINAL 48 WT % U-Al ALLOY TO PLATE-TYPE ALUMINUM RESEARCH REACTOR FUEL ELEMENTS
Technical Report
·
Mon Apr 01 00:00:00 EST 1957
·
OSTI ID:4072060
+1 more
FUEL BEARING FIBERGLAS IN ALUMINUM-BASE FUEL ELEMENTS. Final Report
Technical Report
·
Fri Jun 01 00:00:00 EDT 1962
·
OSTI ID:4072060
THE APPLICATION OF A NOMINAL 48 WT % U-Al ALLOY TO PLATE-TYPE ALUMINUM RESEARCH REACTOR FUEL ELEMENTS
Technical Report
·
Tue Mar 11 00:00:00 EST 1958
·
OSTI ID:4072060
Related Subjects
METALS, CERAMICS, AND OTHER MATERIALS
ALUMINUM
BARRIERS
BURNUP
COLD WORKING
CONFIGURATION
CORROSION
DIFFUSION
DUCTILITY
EXPANSION
FORGING
FUEL CANS
FUEL ELEMENTS
HEAT TREATMENTS
IRRADIATION
LAYERS
MATERIALS TESTING
NICKEL
PHASE DIAGRAMS
PLATES
RADIATION EFFECTS
REACTORS
ROLLING
SURFACES
TENSILE PROPERTIES
URANIUM
WEAR
ALUMINUM
BARRIERS
BURNUP
COLD WORKING
CONFIGURATION
CORROSION
DIFFUSION
DUCTILITY
EXPANSION
FORGING
FUEL CANS
FUEL ELEMENTS
HEAT TREATMENTS
IRRADIATION
LAYERS
MATERIALS TESTING
NICKEL
PHASE DIAGRAMS
PLATES
RADIATION EFFECTS
REACTORS
ROLLING
SURFACES
TENSILE PROPERTIES
URANIUM
WEAR