HIGH ENERGY RATE EXTRUSION. Interim Technical Progress Report No. 3, Phase III, April 1 to June 30, 1961
Technical Report
·
OSTI ID:4003984
Problems with punches and dies, and the need for effective lubrication are discussed. The 90 and 120 deg orifices were found more efficient for extruding plain carbon steel, 4340 steel, 304 stainless, and the titanium alloy. A method for determining Dynapak energy and impact velocity is presented. (auth)
- Research Organization:
- Westinghouse Electric Corp. Materials Manufacturing Dept., Blairsville, PEnna.
- DOE Contract Number:
- AF33(600)-41948
- NSA Number:
- NSA-15-026509
- OSTI ID:
- 4003984
- Report Number(s):
- ASC-TR-7-882(III)
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-61
- Country of Publication:
- United States
- Language:
- English
Similar Records
HIGH ENERGY RATE EXTRUSION. Interim Technical Progress Report No. 1, September 23, 1960 to January 1961
INVESTIGATION OF HYDROSTATIC EXTRUSION. Interim Technical Engineering Report No. 1, June 2, 1961-August 31, 1961
COLUMBIUM AND COLUMBIUM ALLOY EXTRUSION PROGRAM. PHASE III: DEVELOPMENT OF THE EXTRUSION OPERATION. Interim Report IV, February 28, 1961-August 28, 1961
Technical Report
·
Wed Feb 01 00:00:00 EST 1961
·
OSTI ID:4003984
INVESTIGATION OF HYDROSTATIC EXTRUSION. Interim Technical Engineering Report No. 1, June 2, 1961-August 31, 1961
Technical Report
·
Fri Sep 01 00:00:00 EDT 1961
·
OSTI ID:4003984
COLUMBIUM AND COLUMBIUM ALLOY EXTRUSION PROGRAM. PHASE III: DEVELOPMENT OF THE EXTRUSION OPERATION. Interim Report IV, February 28, 1961-August 28, 1961
Technical Report
·
Mon Aug 28 00:00:00 EDT 1961
·
OSTI ID:4003984