Amphoteric behavior and precipitation of Ge dopants in InP
- Center for Advanced Materials, Materials Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, California 94720 (United States)
We have directly correlated the electrical behavior, the impurity lattice site location, ion damage, and the local bonding environments of Ge-dopant ions implanted into InP. We have found that after rapid thermal annealing the free electron concentration in the samples implanted at room temperature (RT) are always higher than those implanted at liquid nitrogen temperature (LNT). Although the macroscopic structure seems to be insensitive to the implantation temperature, significantly more local disorder is created in the LNT implanted amorphous layers. Moreover, the amphoteric bonding structure of the Ge atoms is found to be well established already in the as-implanted amorphous InP. After high temperature annealing ({approx_gt}800{degree}C), the Ge atoms rearrange locally with more of the Ge substituting the In site than the P site resulting in {ital n}-type conductivity. The solid solubility of Ge in the InP is measured to be {approximately}1.4{endash}1.6{times}10{sup 20}/cm{sup 3} while the free electron concentration is estimated to saturate at {approximately}3.4{times}10{sup 19}/cm{sup 3}. The relatively low electron concentration can be explained by Ge precipitation and the compensation of Ge{sub In} donors by Ge{sub P} acceptors in the RT implanted case. The further reduction in electron concentration in the LNT implanted samples is believed to be related to the high residual damage found in these samples. The high solubility of Ge in InP can be attributed to the availability of two possible sublattice sites for the dopant and the compensation of the local strains due to the amphoteric substitution of the Ge. The concentration ratio of the Ge{sub In} to Ge{sub P} determined in the heavily implanted material has been used to estimate the difference in the formation energy of Ge substituting those two different sites.
- Research Organization:
- Lawrence Berkeley National Lab. (LBNL), Berkeley, CA (United States)
- DOE Contract Number:
- AC03-76SF00098
- OSTI ID:
- 385640
- Journal Information:
- Journal of Applied Physics, Vol. 80, Issue 9; Other Information: PBD: Nov 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Direct observation of the amphoteric behavior of Ge in InP modified by P co-implantation
Electrical activation and local structure of Se atoms in ion-implanted indium phosphide