Leaching of both calcium hydroxide and C-S-H from cement paste: Modeling the mechanical behavior
- Commissariat a l`Energie Atomique, Gif-sur-Yvette (France). CEN Saclay
- INSA-UPS Genie Civil Complexe Scientifique de Rangueil, Toulouse (France). Lab. Materiaux et Durabilite des Constructions
This paper deals with the effect of the leaching process of cement based materials on their mechanical properties. This process induces mainly a total leaching of Ca(OH){sub 2} and a progressive decalcification of C-S-H which leads to a gradient of C/S ratio in the leaching zone. In a previous work, the authors venture the hypothesis that the dissolution of calcium hydroxide was the essential parameter governing both decrease in strength and increase in porosity in the case of a paste sample made with an OPC cement which leads to a 20% content of calcium. In order to quantify the effect of the decrease of C/S ratio in C-S-H, the authors have performed experiments on paste samples with the admixture of silica fume to reduce the content of calcium hydroxide and thus emphasize the effect of C/S ratio decrease of the C-S-H. The leaching process was achieved by the use of a 50% concentrate solution of ammonium nitrate. Compression tests were conducted on micro-cylinder samples (10, 12, 14, 20 and 30 mm of diameter) because of the slow kinetics of degradation due to the leaching. The deterioration of the cement paste and the mortar exposed to the action of the ammonium nitrate was indicated by a peripheral zone of less resistance. The experimental results allow the modeling of the mechanical behavior of cement pastes in relation to the ratio of degraded area over total area of the sample A{sub d}/A{sub t}. The model thus defined allows separation of the effect of calcium hydroxide leaching and C-S-H leaching, and shows the importance of the first one. The current research program tries to characterize the deterioration of the mechanical properties of the concrete surrounding radioactive wastes, due to the water flow during storage.
- OSTI ID:
- 377992
- Journal Information:
- Cement and Concrete Research, Vol. 26, Issue 8; Other Information: PBD: Aug 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Investigation of the changes in microstructure and transport properties of leached cement pastes accounting for mix composition
Influence of the Ca/Si ratio of the C–S–H phase on the interaction with sulfate ions and its impact on the ettringite crystallization pressure