Evaluation of pitting corrosion resistance of high-alloyed stainless steels welds for FGD plants in Korea
- Hyundai Heavy Industries Co., Ltd., Ulsan (Korea, Republic of). Hyundai Industrial Research Inst.
For successful application of high-alloyed stainless steels for Flue Gas Desulfurization (FGD) plants, pitting corrosion resistance of arc welds of N-added 6%Mo austenitic stainless steels (UNS N 08367) and super duplex stainless steels (UNS S 32550) made with various filler metals were evaluated using the Green Death solution. For Gas Tungsten Arc (GTA) and Gas Metal Arc (GMA) welds of N 08367, Critical Pitting Temperature (CPT) of base metal was 65--70 C, whereas weld made by ERNiCrMo-3 filler metal yielded CPT of 50 C. Welds made by ERNiCrMo-10 or ERNiCrMo-4 filler metals showed CPT of 60--65 C and 65--70C, respectively. For GTA and GMA welds of S 32550, CPT of welds made by ERNiCrMo-3 was 45--50 C, indicating that the filler metal can provide pitting corrosion resistance matching the S 32550 alloy. Thus, a proper pitting corrosion resistance of weldments of high-alloy stainless steels can be achieved by selecting filler metals having at least +10 higher Pitting Resistance Equivalent Number (PRE{sub N}) value than the base metal regardless of the type of arc welding process. The over-alloyed filler metals would compensate preferential segregation of Cr, MO along the dendrite boundary, which made the dendrite core more susceptible to pitting. Nitrogen addition to the GTA welds of N 08367 made with ERNiCrMo-3 failed to improve pitting corrosion resistance, which was attributed to the precipitation of nitrogen in the weld metal in the form of Nb-nitride.
- OSTI ID:
- 350055
- Report Number(s):
- CONF-980316-; TRN: IM9925%%403
- Resource Relation:
- Conference: Corrosion `98, San Diego, CA (United States), 22-27 Mar 1998; Other Information: PBD: 1998; Related Information: Is Part Of Corrosion `98: 53. annual conference and exposition, proceedings; PB: [6600] p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Performance of high molybdenum superaustenitic stainless steel welds in harsh chloride environments
Influence of nitrogen in the shielding gas on corrosion resistance of duplex stainless steel welds