On the fatigue behavior of {gamma}-based titanium aluminides: Role of small cracks
- Lawrence Berkeley National Lab., CA (United States). Materials Sciences Div.
Gamma-TiAl based alloys have recently received attention for potential elevated temperature applications in gas-turbine engines. However, although expected critical crack sizes for some targeted applications (e.g., gas-turbine engine blades) may be less than {approximately}500 {micro}m, most fatigue-crack growth studies to date have focused on the behavior of large (on the order of a few millimeters) through-thickness cracks. Since successful implementation of damage-tolerant life-prediction methodologies requires that the fatigue properties be understood for crack sizes representative of those seen in service conditions, the present work is focused on characterizing the initiation and growth behavior of small (a {approximately}15--300 {micro}m) fatigue cracks in a {gamma}-TiAl based alloy, of composition Ti-47Al-2Nb-2Cr-0.2B (at.%), with both duplex (average grain size of {approximately}17 {micro}m) and refined lamellar (average colony size of {approximately}145 {micro}m) microstructures. Results are compared to the behavior of large (a > 5 mm), through-thickness cracks from a previous study. Superior crack initiation resistance is observed in the duplex microstructure, with no cracks nucleating after up to 500,000 cycles at maximum stress levels (R = 0.1) in excess of the monotonic yield stress, {sigma}{sub y}. Comparatively, in the lamellar microstructure cracks nucleated readily at applied maximum stresses below the yield stress (85% {sigma}{sub y}) after as few as 500 cycles. In terms of crack growth, measurements for small fatigue cracks in the duplex and lamellar microstructures showed that both microstructures have comparable intrinsic fatigue-crack growth resistance in the presence of small flaws. This observation contrasts previous comparisons of large-crack data, where the lamellar structure showed far superior fatigue-crack growth resistance than the duplex structure. Such small-crack effects are examined both in terms of similitude (i.e., crack tip shielding) and continuum (i.e., biased microstructural sampling) limitations of traditional linear elastic fracture mechanics.
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC03-76SF00098
- OSTI ID:
- 329080
- Journal Information:
- Acta Materialia, Vol. 47, Issue 3; Other Information: PBD: 5 Feb 1999
- Country of Publication:
- United States
- Language:
- English
Similar Records
Fatigue and fracture behavior of a fine-grained lamellar TiAl alloy
A first report on the creep deformation and damage behavior of a fine grained fully transformed lamellar gamma TiAl alloy