Structural transformations in the Stranski-Krastanov growth of Mg on Mo(001)
- Department of Physics, Lakehead University, Thunder Bay, Ontario, P7B 5E1 (CANADA)
- Environmental Molecular Sciences Laboratory, Pacific Northwest National Laboratory, Richland, Washington 99352 (United States)
The epitaxy of Mg, a hexagonal-closed-packed (hcp) metal in the bulk, onto a room-temperature body-centered-cubic Mo(001) substrate is investigated. A Stranski-Krastanov, layer by layer followed by islands, growth mode is observed including the initial stabilization of a metastable face-centered-cubic (fcc) phase of Mg. Layer by layer growth persists for four layers. During growth of the first and second layer the highly corrugated surface potential and lattice mismatch both act to limit island size, and growth proceeds via nucleation and growth of small two-dimensional islands. Third- and fourth-layer growth proceeds by step flow. The increase in the diffusion constant necessary for step flow may be aided by the presence of a stress relieved c(2{times}2) surface reconstruction in this regime. The reconstruction may result from a buckling of the Mg lattice to conform to the smaller Mo(001) spacing. Measurement of atomic step heights confirms the growth of fcc Mg(001). Beyond four layers a transition to three-dimensional (3D) island growth occurs. Associated with this transition is a change in crystal structure. The 3D islands exhibit hexagonal symmetry with two domains rotated by 30{degree} with respect to one another. Measurement of emergent screw dislocations at the surface of the islands confirms the growth of hcp Mg(0001). Evidence of edge dislocations aligned with steps in the underlying Mo substrate are also observed. {copyright} {ital 1999} {ital The American Physical Society}
- OSTI ID:
- 295546
- Journal Information:
- Physical Review, B: Condensed Matter, Vol. 59, Issue 3; Other Information: PBD: Jan 1999
- Country of Publication:
- United States
- Language:
- English
Similar Records
Stranski-Krastanov growth in Mg{sub 0.37}Zn{sub 0.63}O/ZnO heteroepitaxy: Self-organized nanodots and local composition separation
In situ revelation of a zinc-blende InN wetting layer during Stranski-Krastanov growth on GaN(0001) by molecular-beam epitaxy