A new hybrid two-zone/crucible furnace process for the growth of epitaxial Tl{sub 2}Ba{sub 2}CaCu{sub 2}O{sub 8} superconducting films
- Sandia National Laboratories, Albuquerque, New Mexico 87185-1421 (United States)
Epitaxial Tl{sub 2}Ba{sub 2}CaCu{sub 2}O{sub 8} (Tl-2212) films {approximately}5500 {Angstrom} thick are grown on LaAlO{sub 3}(100) substrates using a new hybrid two-zone/crucible furnace process enabling precise control of thallination. This method combines the best features of both conventional crucible and two-zone processing for the first time: superb film properties and reduced handling of hazardous Tl-oxide powders. Single-phase, highly {ital c}-axis oriented Tl-2212 films are grown with smooth morphology, Meissner transition {approximately}103 K, and critical current density {approximately}1.1{times}10{sup 7}A/cm{sup 2} at 5 K for twenty consecutive runs without having to change or add to the Tl-oxide source. {copyright} {ital 1998 Materials Research Society.}
- Research Organization:
- Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 292709
- Journal Information:
- Journal of Materials Research, Vol. 13, Issue 12; Other Information: PBD: Dec 1998
- Country of Publication:
- United States
- Language:
- English
Similar Records
Importance of controlling the Tl-oxide partial pressure throughout the processing of TlBa{sub 2}CaCu{sub 2}O{sub 7} thin films
LaNiO{sub 3} buffer layers for high critical current density YBa{sub 2}Cu{sub 3}O{sub 7{minus}{delta}} and Tl{sub 2}Ba{sub 2}CaCu{sub 2}O{sub 8{minus}{delta}} films
Related Subjects
THALLIUM COMPOUNDS
BARIUM COMPOUNDS
CALCIUM COMPOUNDS
COPPER COMPOUNDS
OXYGEN COMPOUNDS
SUPERCONDUCTING FILMS
HIGH-TC SUPERCONDUCTORS
THALLIUM OXIDES
BARIUM OXIDES
CALCIUM OXIDES
COPPER OXIDES
EPITAXY
CRYSTAL GROWTH METHODS
CRYSTAL GROWTH
CRYSTAL STRUCTURE
TEXTURE
CRITICAL CURRENT
TRANSITION TEMPERATURE