Fabrication of TiB{sub 2} and TiB{sub 2}/FeB composites by mechanically activated borothermic reduction of ilmenite
Journal Article
·
· Journal of Materials Research
- Department of Applied Mathematics and Electronic Materials Engineering, Research School of Physical Sciences and Engineering, The Australian National University, Canberra, ACT 0200 (Australia)
- Department of Electronic Materials Engineering, Research School of Physical Sciences and Engineering, The Australian National University, Canberra, ACT 0200 (Australia)
TiB{sub 2} and TiB{sub 2}/FeB composites have been formed at temperatures below 1000{degree}C, directly from ilmenite sand by reaction with amorphous boron. The structural transformations occurring during high-energy mechanical milling pretreatment and subsequent annealing of different mixtures of the constituents have been studied. On heating at temperature below 800{degree}C, complete borothermic reduction of the ilmenite structure is accomplished. The mixture so obtained with ilmenite-boron ratio equal to 1/6 undergoes a sequence of reactions on further heating to form TiB{sub 2}, FeB, and the amorphous phase B{sub 2}O{sub 2}. {copyright} {ital 1996 Materials Research Society.}
- OSTI ID:
- 282875
- Journal Information:
- Journal of Materials Research, Vol. 11, Issue 4; Other Information: PBD: Apr 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Synthesis of TiB sub 2 by the borothermic/carbothermic reduction of TiO sub 2 with B sub 4 C
Mechanical enhancement of the carbothermic formation of TiB{sub 2}
Aluminothermic reaction path in the synthesis of a TiB{sub 2}-Al{sub 2}O{sub 3} composite
Journal Article
·
Tue Nov 01 00:00:00 EST 1988
· Advanced Ceramic Materials; (USA)
·
OSTI ID:282875
Mechanical enhancement of the carbothermic formation of TiB{sub 2}
Journal Article
·
Sat Jan 01 00:00:00 EST 2000
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science
·
OSTI ID:282875
Aluminothermic reaction path in the synthesis of a TiB{sub 2}-Al{sub 2}O{sub 3} composite
Journal Article
·
Tue Jul 01 00:00:00 EDT 1997
· Journal of Materials Research
·
OSTI ID:282875