Nature of the real structure of graphite-like BN and its transformation into a wurtsite modification under impact compression
Journal Article
·
· Powder Metallurgy and Metal Ceramics
- Institute of Materials Science Problems, Kiev (Ukraine); and others
The dependence of the interlayer distance d on the degree of unidimensional disorder {gamma} in graphite-like BN was determined. It was established that d = 0.33273 {plus_minus} 0.00006 nm at 20{degrees} in the perfectly ordered structure ({gamma}=O); the value of d increased uniformly with increase of {gamma}, and at {gamma} = 1 it equals 0.343 {plus_minus} 0.001 nm. It was also established that the yield of wurtsite phase produced by impact compression of the graphite-like modification sharply decreases with increase of {gamma}, and for {gamma} {ge} 0.2 it becomes equal to zero. This result is explained in terms of the nature of martensitic transformatons in layered structures.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 237607
- Journal Information:
- Powder Metallurgy and Metal Ceramics, Vol. 33, Issue 9-10; Other Information: PBD: Mar 1995; TN: Translated from Poroshkovaya Metallurgiya; Nos. 9-10, 62-66(Sep-Oct 1994)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Compressed glassy carbon maintaining graphite-like structure with linkage formation between graphene layers
Ab initio study of graphite. -->. diamondlike transitions in BN
Structural studies of ceramics based on detonation-wave-treated graphite-like boron nitride
Journal Article
·
Fri May 17 00:00:00 EDT 2019
· Scientific Reports
·
OSTI ID:237607
Ab initio study of graphite. -->. diamondlike transitions in BN
Journal Article
·
Thu Sep 15 00:00:00 EDT 1988
· Phys. Rev. B: Condens. Matter; (United States)
·
OSTI ID:237607
+1 more
Structural studies of ceramics based on detonation-wave-treated graphite-like boron nitride
Journal Article
·
Wed Nov 01 00:00:00 EST 1995
· Powder Metallurgy and Metal Ceramics
·
OSTI ID:237607