Interaction Between Graphene-Coated SiC Single Crystal and Liquid Copper
- Foundry Research Institute (Poland)
- Institute of Electronic Materials Technology (Poland)
- Politechnika Warszawska Wydział Fizyki (Poland)
The wettability of graphene-coated SiC single crystal (C{sub Gn}/SiC{sup sc}) by liquid Cu (99.99%) was investigated by a sessile drop method in vacuum conditions at temperature of 1100 °C. The graphene layer was produced via a chemical vapor deposition routine using 4H-SiC single crystal cut out from 6″ wafer. A dispensed drop technique combined with a non-contact heating of a couple of materials was applied. The Cu drop was squeezed from a graphite capillary and deposited on the substrate directly in a vacuum chamber. The first Cu drop did not wet the C{sub Gn}/SiC{sup sc} substrate and showed a lack of adhesion to the substrate: the falling Cu drop only touched the substrate forming a contact angle of θ{sub 0} = 121° and then immediately rolled like a ball along the substrate surface. After settling near the edge of the substrate in about 0.15 s, the Cu drop formed an asymmetric shape with the right and left contact angles of different values (θ{sub R} = 86° and θ{sub L} = 70°, respectively), while in the next 30 min, θ{sub R} and θ{sub L} achieved the same final value of ~ 52°. The second Cu drop was put down on the displacement path of the first drop, and immediately after the deposition, it also did not wet the substrate (θ = 123°). This drop kept symmetry and the primary position, but its wetting behavior was unusual: both θ{sub R} and θ{sub L} decreased in 17 min to the value of 23° and next, they increased to a final value of 65°. Visual observations revealed a presence of ~ 2.5-mm-thick interfacial phase layer reactively formed under the second drop. Scanning electron microscopy (SEM) investigations revealed the presence of carbon-enriched precipitates on the top surface of the first Cu drop. These precipitates were identified by the Raman spectroscopy as double-layer graphene. The Raman spectrum taken from the substrate far from the drop revealed the presence of graphene, while that obtained from the first drop displacement path exhibited a decreased intensity of 2D peak. The results of SEM investigations and Raman spectroscopy studies suggest that the presence of graphene layer on the SiC substrate suppresses but does not completely prevent chemical interaction between liquid Cu drop and SiC. Both chemical degradation (etching) and mechanical degradation of the graphene layer during drop rolling due to high adhesion of the Cu drop to the SiC substrate are responsible for mass transfer through the 2nd drop/substrate interface that in turn results in significant changes of structure and chemistry of the drop and the interface.
- OSTI ID:
- 22860508
- Journal Information:
- Journal of Materials Engineering and Performance, Vol. 27, Issue 5; Other Information: Copyright (c) 2018 ASM International; Article Copyright (c) 2018 The Author(s); http://www.springer-ny.com; Country of input: International Atomic Energy Agency (IAEA); ISSN 1059-9495
- Country of Publication:
- United States
- Language:
- English
Similar Records
Combinatorial Cu-Ni Alloy Thin-Film Catalysts for Layer Number Control in Chemical Vapor-Deposited Graphene
Assessing the quality of large-area monolayer graphene grown on liquid copper for size-selective ionic/molecular membrane separations