B{sub 4}C protective coating under irradiation by QSPA-T intensive plasma fluxes
- Troitsk Institute for Innovation and Fusion Research (TRINITI) (Russian Federation)
The effect of the QSPA-T pulsed plasma irradiation on the crystalline boron carbide B{sub 4}C coating was examined. The duration of the rectangular plasma pulses was 0.5 ms with an interval of 5–10 min between pulses. The maximum power density in the central part of plasma stream was 1 GW/m{sup 2}. The coating thickness varied from 20 to 40 μm on different surface areas. Modification of the surface layers and transformation of the coating at elevated temperature under plasma pulse irradiation during four successive series of impulses are described. It is shown that the boron carbide coating withstood the full cycle of tests under irradiation with 100 plasma pulses with peak power density of 1GW/m{sup 2}. Constitutive surface deterioration was not detected and the boron carbide coating kept crystal structure B{sub 4}C throughout the irradiation zone at the surface depth no less 2 μm.
- OSTI ID:
- 22612571
- Journal Information:
- Physics of Atomic Nuclei, Vol. 79, Issue 7; Other Information: Copyright (c) 2016 Pleiades Publishing, Ltd.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1063-7788
- Country of Publication:
- United States
- Language:
- English
Similar Records
Boron carbide coating deposition on tungsten and testing of tungsten layers and coating under intense plasma load
Heat Flux Calculation and Problem of Flaking of Boron Carbide Coatings on the Faraday Screen of the ICRH Antennas During Tore Supra High Power, Long Pulse Operation