Investigation of phonon modes in gallium nitride nanowires deposited by thermal CVD
Gallium nitride nanowires (GaN-NWs) of diameters ranging from 20 to 80 nm were grown on the p-type Si substrate by Thermal Chemical Vapor Deposition (TCVD) using Iron (Fe) catalyst via VLS mechanism. Raman and FTIR spectra reveal the presence of broad transverse optic (TO) and longitudinal optic (LO) phonon peak spreads over 500-600 cm{sup −1} and 720 cm{sup −1} respectively. The detail deconvolution of integrated transverse and longitudinal phonon analysis reveals phonon confinement brought out by incorporation of hydrogen atom. The red shifts of TO and LO phonon peak position indicates nanosized effect. I{sub A1(LO)}/I{sub A1(TO)} increases from 0.073 to 1.0 and their respective fwhm{sub A1(LO)}/fwhm{sub A1(TO)} also increases from 0.71 to 1.31 with increasing H{sub 2} flow rate. E{sub 1}(LO) - E{sub 1}(TO) and A{sub 1}(LO) - A{sub 1}(TO) increases from 173.83 to 190.73 and 184.89 to 193.22 respectively. Apart from this usual TO and LO phonon, we have found Surface Optic (SO) phonon at 671 cm{sup −1} in FTIR spectra. The intensity of PL peak increases with increasing H{sub 2} dilution reveals efficient passivation of defect centre at surface of GaN-NWs.
- OSTI ID:
- 22591076
- Journal Information:
- AIP Conference Proceedings, Vol. 1724, Issue 1; Conference: ETMN-2015: 2. international conference on emerging technologies: Micro to nano 2015, Rajasthan (India), 24-25 Oct 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structural and Optical Properties of InGaN-GaN Nanowire Heterostructures Grown by Molecular Beam Epitaxy
Structural and optical properties of InGaN-GaN nanowire heterostructures grown by molecular beam epitaxy