Photoluminescence of A- and B-site Eu{sup 3+}-substituted (Sr{sub x}Ba{sub 1−x}){sub 2}CaW{sub y}Mo{sub 1−y}O{sub 6} phosphors
- Norwegian University of Science and Technology, Department of Materials Science and Engineering, NO-7491 Trondheim (Norway)
- Norwegian University of Science and Technology, Department of Physics, NO-7491 Trondheim (Norway)
- Université de Toulon, IM2NP UMR 7334 CNRS, P.O. Box 20132, 83957 La Garde Cedex (France)
The photoluminescence of two series of A- and B-site Eu{sup 3+} substituted (Sr{sub x}Ba{sub 1−x}){sub 2}CaW{sub y}Mo{sub 1−y}O{sub 6} double perovskite phosphor materials, (Sr{sub x}Ba{sub 1−x}){sub 1.96}Eu{sub 0.02}K{sub 0.02}CaW{sub y}Mo{sub 1−y}O{sub 6} and (Sr{sub x}Ba{sub 1−x}){sub 2}Ca{sub 0.96}Eu{sub 0.02}Li{sub 0.02}W{sub y}Mo{sub 1−y}O{sub 6} (x and y=0, 0.25, 0.50, 0.75, and 1), were studied systematically as a function of stoichiometry and crystal structure. The Eu{sup 3+} lattice sites controlled by co-doping with either K or Li were confirmed by Raman spectroscopy. The variation in integrated emission intensity and emission colour over the experimental matrix was examined using statistical tools, and the observed trends were rationalized based on the physical and electronic structure of the phosphors. Phosphors with Eu on B-site with maximum Sr content had remarkably higher emission intensities than all other materials, but the emission was more orange than red due to domination of the {sup 5}D{sub 0}–{sup 7}F{sub 1} (595 nm) transition of Eu{sup 3+}. The relative intensities of the {sup 5}D{sub 0}–{sup 7}F{sub 2} (615 nm) and {sup 5}D{sub 0}–{sup 7}F{sub 1} transitions of Eu{sup 3+}, and thus the red-shift of the emission, decreased linearly with increasing Sr content in the A-site Eu-substituted phosphors, and reached a maximum for Sr{sub 1.96}Eu{sub 0.02}K{sub 0.02}CaW{sub 0.25}Mo{sub 0.75}O{sub 6}. A maximum external quantum efficiency of 17% was obtained for the phosphor Sr{sub 2}Ca{sub 0.7}Eu{sub 0.15}Li{sub 0.15}W{sub 0.5}Mo{sub 0.5}O{sub 6} with Eu on B-site. - Highlights: • Systematic study of the photoluminescence of Eu{sup 3+}-doped (Sr{sub x}Ba{sub 1−x}){sub 2}CaW{sub y}Mo{sub 1−y}O{sub 6}. • The Eu{sup 3+} lattice sites were confirmed by Raman spectroscopy. • A large parameter space was investigated using statistical tools. • A maximum external QE of 17% was obtained for Sr{sub 2}Ca{sub 0.7}Eu{sub 0.15}Li{sub 0.15}W{sub 0.5}Mo{sub 0.5}O{sub 6}.
- OSTI ID:
- 22584056
- Journal Information:
- Journal of Solid State Chemistry, Vol. 237; Other Information: Copyright (c) 2016 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Sr{sub 2}CaW{sub x}Mo{sub 1−x}O{sub 6}:Eu{sup 3+}, Li{sup +}: An emission tunable phosphor through site symmetry and excitation wavelength
Synthesis, phase transition and photoluminescence studies on Eu{sup 3+}-substituted double perovskites-A novel orange-red phosphor for solid-state lighting