Refractive index and compressibility of LiAlSi{sub 3}O{sub 8} glass in the pressure range up to 6.0 GPa
Highlights: • Refractive index and the compressibility of LiAlSi{sub 3}O{sub 8} glass are obtained. • Among Li(Na,K)AlSi{sub 3}O{sub 8} glasses LiAlSi{sub 3}O{sub 8} glass has the lowest compressibility. • Degree of depolymerization (NBO/T = 0.31) for LiAlSi{sub 3}O{sub 8} glass was calculated. • NBO/T = 0.31 indicates a high content of NBOs atoms and Al in LiAlSi{sub 3}O{sub 8} glass. • Proposed reaction corresponds to the condition of the existence of ∼9% Al. - Abstract: The refractive index and the relative changes in the density for LiAlSi{sub 3}O{sub 8} glass in the pressure range up to 6.0 GPa were obtained using a polarization-interference microscope and an apparatus with diamond anvils. The results were compared with the previous data for the NaAlSi{sub 3}O{sub 8} and KAlSi{sub 3}O{sub 8} glasses. The compressibility of glasses increases in a series of alkali metal cations Li{sup +}, Na{sup +}, K{sup +}. From the previously found dependence of the compressibility (at P = 4.0 GPa) on the degree of depolymerization the value of NBO/T = 0.31 for LiAlSi{sub 3}O{sub 8} glass was calculated. A high degree of depolymerization of the LiAlSi{sub 3}O{sub 8} glass indicates not only a high content of NBOs atoms in the structural network, but also the presence of highly coordinated aluminum (according to the literature data ∼9%). The proposed schematic reaction for the formation of different structural groups corresponds to the condition of the existence of 9% highly coordinated aluminum.
- OSTI ID:
- 22581436
- Journal Information:
- Materials Research Bulletin, Vol. 74; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structural environments of incompatible elements in silicate glass/melt systems: 1. Zirconium at trace levels
High temperature liquid and glass heat contents and the heats of fusion of diopside, albite, sanidine and nepheline
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
36 MATERIALS SCIENCE
ALUMINIUM SILICATES
CATIONS
COMPRESSIBILITY
DEPOLYMERIZATION
ELASTICITY
EQUATIONS OF STATE
LITHIUM COMPOUNDS
LITHIUM IONS
POLARIZATION
POTASSIUM COMPOUNDS
POTASSIUM IONS
PRESSURE DEPENDENCE
PRESSURE RANGE GIGA PA
REFRACTIVE INDEX
SODIUM COMPOUNDS
SODIUM IONS