Highly conducting divalent Mg{sup 2+} cation solid electrolytes with well-ordered three-dimensional network structure
A three-dimensionally well-ordered NASICON-type Mg{sup 2+} cation conductor, (Mg{sub x}Hf{sub 1−x}){sub 4/(4−2x)}Nb(PO{sub 4}){sub 3}, was firstly developed by partial substitution of lower valent Mg{sup 2+} cation onto the Hf{sup 4+} sites in a HfNb(PO{sub 4}){sub 3} solid to realize high Mg{sup 2+} cation conductivity even at moderate temperatures. Due to the formation of well-ordered NASICON-type structure, both the high Mg{sup 2+} cation conductivity below 450 °C and the low activation energy for Mg{sup 2+} cation migration was successfully realized for the (Mg{sub 0.1}Hf{sub 0.9}){sub 4/3.8}Nb(PO{sub 4}){sub 3} solid. Pure Mg{sup 2+} cation conduction in the NASICON-type (Mg{sub 0.1}Hf{sub 0.9}){sub 4/3.8}Nb(PO{sub 4}){sub 3} solid was directly and quantitatively demonstrated by means of two kinds of dc electrolysis. - Graphical abstract: Image of the Mg{sup 2+} cation conduction in NASICON-type (Mg{sub 0.1}Hf{sub 0.9}){sub 4/3.8}Nb(PO{sub 4}){sub 3} and its Mg{sup 2+} conductivity. - Highlights: • We develop a three-dimensionally well-ordered NASICON-type Mg{sup 2+} cation conductor. • A high magnesium cation conductivity is realized even at moderate temperatures. • Divalent magnesium cation conduction is demonstrated directly and quantitatively.
- OSTI ID:
- 22577780
- Journal Information:
- Journal of Solid State Chemistry, Vol. 235; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Catalytic Activity of Li{sub 1+x}Hf{sub 2–x}In{sub x}(PO{sub 4}){sub 3}-Based NASICON-Type Materials for Ethanol Conversion Reactions
Distribution and mobility of lithium in NASICON-type Li1-xTi2-xNbx(PO4)3 (0 ≤ x ≤ 0.5) compounds