Title: Influence of PbCl{sub 2} content in PbI{sub 2} solution of DMF on the absorption, crystal phase, morphology of lead halide thin films and photovoltaic performance in planar perovskite solar cells

Abstract

In this paper, the influence of PbCl{sub 2} content in PbI{sub 2} solution of DMF on the absorption, crystal phase and morphology of lead halide thin films was systematically investigated and the photovoltaic performance of the corresponding planar perovskite solar cells was evaluated. The result revealed that the various thickness lead halide thin film with the small sheet-like, porous morphology and low crystallinity can be produced by adding PbCl{sub 2} powder into PbI{sub 2} solution of DMF as a precursor solution. The planar perovskite solar cell based on the 300-nm-thick CH{sub 3}NH{sub 3}PbI{sub 3−x}Cl{sub x} thin film by the precursor solution with the mixture of 0.80 M PbI{sub 2} and 0.20 M PbCl{sub 2} exhibited the optimum photoelectric conversion efficiency of 10.12% along with an open-circuit voltage of 0.93 V, a short-circuit photocurrent density of 15.70 mA cm{sup −2} and a fill factor of 0.69. - Graphical abstract: The figure showed the surface and cross-sectional SEM images of lead halide thin films using the precursor solutions: (a) 0.80 M PbI{sub 2}, (b) 0.80 M PbI{sub 2}+0.20 M PbCl{sub 2}, (c) 0.80 M PbI{sub 2}+0.40 M PbCl{sub 2}, and (d) 0.80 M PbI{sub 2}+0.60 M PbCl{sub 2}. With the increase ofmore » the PbCl{sub 2} content in precursor solution, the size of the lead halide nanosheet decreased and the corresponding thin films gradually turned to be porous with low crystallinity. - Highlights: • Influence of PbCl{sub 2} content on absorption, crystal phase and morphology of thin film. • Influence of perovskite film thickness on photovoltaic performance of solar cell. • Lead halide thin film with small sheet-like, porous morphology and low crystallinity. • Planar solar cell with 300 nm-thick perovskite thin film achieved PCE of 10.12%.« less

Authors:
; ; ; ;
Publication Date:
OSTI Identifier:
22573922
Resource Type:
Journal Article
Journal Name:
Journal of Solid State Chemistry
Additional Journal Information:
Journal Volume: 231; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); Journal ID: ISSN 0022-4596
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; ABSORPTION; EFFICIENCY; ELECTRIC POTENTIAL; ELECTRICAL FAULTS; LEAD; LEAD CHLORIDES; LEAD IODIDES; NANOSTRUCTURES; PERFORMANCE; PEROVSKITE; PHOTOVOLTAIC EFFECT; POROUS MATERIALS; POWDERS; PRECURSOR; SCANNING ELECTRON MICROSCOPY; SOLAR CELLS; SOLUTIONS; SURFACES; THICKNESS; THIN FILMS

Citation Formats

Wang, Mao, Shi, Chengwu, Zhang, Jincheng, Wu, Ni, and Ying, Chao. Influence of PbCl{sub 2} content in PbI{sub 2} solution of DMF on the absorption, crystal phase, morphology of lead halide thin films and photovoltaic performance in planar perovskite solar cells. United States: N. p., 2015. Web. doi:10.1016/J.JSSC.2015.08.002.
Wang, Mao, Shi, Chengwu, Zhang, Jincheng, Wu, Ni, & Ying, Chao. Influence of PbCl{sub 2} content in PbI{sub 2} solution of DMF on the absorption, crystal phase, morphology of lead halide thin films and photovoltaic performance in planar perovskite solar cells. United States. https://doi.org/10.1016/J.JSSC.2015.08.002
Wang, Mao, Shi, Chengwu, Zhang, Jincheng, Wu, Ni, and Ying, Chao. Sun . "Influence of PbCl{sub 2} content in PbI{sub 2} solution of DMF on the absorption, crystal phase, morphology of lead halide thin films and photovoltaic performance in planar perovskite solar cells". United States. https://doi.org/10.1016/J.JSSC.2015.08.002.
@article{osti_22573922,
title = {Influence of PbCl{sub 2} content in PbI{sub 2} solution of DMF on the absorption, crystal phase, morphology of lead halide thin films and photovoltaic performance in planar perovskite solar cells},
author = {Wang, Mao and Shi, Chengwu and Zhang, Jincheng and Wu, Ni and Ying, Chao},
abstractNote = {In this paper, the influence of PbCl{sub 2} content in PbI{sub 2} solution of DMF on the absorption, crystal phase and morphology of lead halide thin films was systematically investigated and the photovoltaic performance of the corresponding planar perovskite solar cells was evaluated. The result revealed that the various thickness lead halide thin film with the small sheet-like, porous morphology and low crystallinity can be produced by adding PbCl{sub 2} powder into PbI{sub 2} solution of DMF as a precursor solution. The planar perovskite solar cell based on the 300-nm-thick CH{sub 3}NH{sub 3}PbI{sub 3−x}Cl{sub x} thin film by the precursor solution with the mixture of 0.80 M PbI{sub 2} and 0.20 M PbCl{sub 2} exhibited the optimum photoelectric conversion efficiency of 10.12% along with an open-circuit voltage of 0.93 V, a short-circuit photocurrent density of 15.70 mA cm{sup −2} and a fill factor of 0.69. - Graphical abstract: The figure showed the surface and cross-sectional SEM images of lead halide thin films using the precursor solutions: (a) 0.80 M PbI{sub 2}, (b) 0.80 M PbI{sub 2}+0.20 M PbCl{sub 2}, (c) 0.80 M PbI{sub 2}+0.40 M PbCl{sub 2}, and (d) 0.80 M PbI{sub 2}+0.60 M PbCl{sub 2}. With the increase of the PbCl{sub 2} content in precursor solution, the size of the lead halide nanosheet decreased and the corresponding thin films gradually turned to be porous with low crystallinity. - Highlights: • Influence of PbCl{sub 2} content on absorption, crystal phase and morphology of thin film. • Influence of perovskite film thickness on photovoltaic performance of solar cell. • Lead halide thin film with small sheet-like, porous morphology and low crystallinity. • Planar solar cell with 300 nm-thick perovskite thin film achieved PCE of 10.12%.},
doi = {10.1016/J.JSSC.2015.08.002},
url = {https://www.osti.gov/biblio/22573922}, journal = {Journal of Solid State Chemistry},
issn = {0022-4596},
number = ,
volume = 231,
place = {United States},
year = {2015},
month = {11}
}