Due to the worldwide shortage of helium 3, Boron-lined proportional counters are developed intensively by several groups. Up to now, thin boron containing layers for neutron detectors are essentially produced by sputtering of boron carbide (B{sub 4}C). This technology provides high quality films but it is slow and expensive. Our paper describes a novel and inexpensive technology for producing boron layers. This technology is based on chemical synthesis of boron 10 nanoparticles, and on electrophoretic deposition of these particles on metallic plates, or on metallic pieces with more complex shapes. The chemical synthesis consists in: - Heating boron 10 with lithium up to 700 deg. C under inert atmosphere: an intermetallic compound, LiB, is produced; - Hydrolysing this intermetallic compound: LiB + H{sub 2}O → B + Li{sup +} + OH{sup -} + 1/2H{sub 2}, where B is under the form of nanoparticles; - Purifying the suspension of boron nanoparticles in water, from lithium hydroxide, by successive membrane filtrations; - Evaporating the purified suspension, in order to get a powder of nanoparticles. The obtained nanoparticles have size around 300 nm, with a high porosity, of about 50%. This particle size is equivalent to about 150 nm massive particles. The nanoparticles are then put into suspension in a specific solvent, in order to perform deposition on metallic surfaces, by electrophoretic method. The solvent is chosen so that it is not electrolysed even under voltages of several tens of volts. An acid is dissolved into the solvent, so that the nanoparticles are positively charged. Deposition is performed on the cathode within about 10 min. The cathode could be an aluminium plate, or a nickel coated aluminium plate. Homogeneous deposition may also be performed on complex shapes, like grids in a Multigrid detector. A large volume of pieces, can be coated with a Boron-10 film in a few hours. The thickness of the layer can be adjusted according to the required neutron detection characteristics, between 0,5 to 5 μm (equivalent to 0,25 to 2.5 massive layer). The thickness is homogenous within a ±20% range. The layer is an almost pure {sup 10}B layer (90%). The ratio of the amount of deposed boron 10 to the amount of raw boron 10 used is more than 80%. Hence, another advantage of this technique is that Boron 10 will be deposited on the cathodes only, without loss of this expensive material. 2 grids of a Multi-Grid detector have been coated with pure Boron by using this technique. The film structure has been analysed with a microscope and the detector has been tested on a monochromatic neutron beam line. Preliminary results will be shown. (authors)
- Research Organization:
- Institute of Electrical and Electronics Engineers - IEEE, 3 Park Avenue, 17th Floor, New York, N.Y. 10016-5997 (United States)
- OSTI ID:
- 22531294
- Report Number(s):
- ANIMMA-2015-IO-244; TRN: US16V0474102235
- Resource Relation:
- Conference: ANIMMA 2015: 4. International Conference on Advancements in Nuclear Instrumentation Measurement Methods and their Applications, Lisboa (Portugal), 20-24 Apr 2015; Other Information: Country of input: France
- Country of Publication:
- United States
- Language:
- English
Similar Records
REACTOR INSTRUMENTATION AND CONTROL PROGRESS REPORT NO. 77
Recent development of the Multi-Grid detector for large area neutron scattering instruments
Related Subjects
36 MATERIALS SCIENCE
BORON 10
BORON CARBIDES
CATHODES
ELECTROPHORESIS
INTERMETALLIC COMPOUNDS
LITHIUM HYDROXIDES
MEMBRANES
MICROSCOPES
MONOCHROMATIC RADIATION
NANOPARTICLES
NEUTRON BEAMS
NEUTRON DETECTION
NEUTRON DETECTORS
PROPORTIONAL COUNTERS
THIN FILMS