Magnetocaloric properties of rare-earth substituted DyCrO{sub 3}
- Material Science and Engineering Department, University of Connecticut, Storrs, Connecticut 06269 (United States)
Recently, there has been a focus on the need for efficient refrigeration technology without the use of expensive or harmful working fluids, especially at temperatures below 30 K. Solid state refrigeration, based on the magnetocaloric effect, provides a possible solution to this problem. The rare-earth chromites (RCrO{sub 3}), especially DyCrO{sub 3}, with its large magnetic moment dysprosium ion, are potential candidates for such an application. The Dy{sup 3+} ordering transition at low temperatures (<10 K) likely causes a large magnetocaloric response in this material. This study investigates the possibility of tuning the magnetocaloric properties through the use of rare-earth substitution. Both Y{sup 3+} and Ho{sup 3+} substitutions were found to decrease the magnetocaloric response by disrupting the R{sup 3+} ordering. Whereas Er{sup 3+} substitution was found to increase the magnetocaloric response, likely due to an increase in the R{sup 3+} ordering temperature. The large magnetocaloric entropy change of Er{sup 3+} substituted DyCrO{sub 3} (10.92 J/kg K with a relative cooling power of 237 J/kg at 40 kOe and 5 K) indicates that this material system is well suited for low temperature (<30 K) solid state refrigeration applications.
- OSTI ID:
- 22494642
- Journal Information:
- Journal of Applied Physics, Vol. 118, Issue 4; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Gd substitution on the structural, magnetic, and magnetocaloric properties of HoCrO 3
Enhancement in magnetocaloric properties of holmium chromite by gadolinium substitution