Metal (Fe, Co, Ni) supported on different aluminas as Fischer-Tropsch catalyst
- Chemistry Education Study Program, Universitas Halu Oleo, Jl. HEA Mokodompit, Kendari 93232 (Indonesia)
- Inorganic and Physical Chemistry Division, Departement of Chemistry, Institut Teknologi Bandung, Jl. Ganesha 10, Bandung 40132 (Indonesia)
- Center of Excellence on Catalysis and Catalytic Reaction Engineering, Department of Chemical Engineering, Chulalongkorn University, 254 Phayathai Road, Bangkok 10330 (Thailand)
This research aimed to compare the physico-chemical properties of the same metal M (M = iron, cobalt, nickel) supported on aluminas with different morphology and pore size as Fischer-Tropsch catalyst. The aluminas applied as support were alumina synthesized through hydrothermal process, alumina formed by pretreatment of catapal and commercial alumina which named as Ahy, Aca, and Aco respectively. Ahy has uniform morphology of nanotubes while Aca and Aco showed non-uniform morphology of particle lumps. The particle lumps of Aca were larger than those of Aco. Ahy, Aca, and Aco respectively has average pore diameter of 2.75, 2.86 and 2.9 nm. Metals were deposited on the supports by incipient-wetness impregnation method. The catalysts were characterized by XRD, H{sub 2}-TPR, and H{sub 2} chemisorption. Catalyst acitivity test for Fischer-Tropsch reaction was carried out in a micro reactor at 200 °C and 1 atm, and molar ratio of H{sub 2}/CO = 2:1. The metal oxide particle size increased in the order M/Aco < M/Aca < M/Ahy. The catalysts reducibility also increased according to the order M/Aco < M/Aca < M/Ahy suggesting that the larger metal oxide particles are more reducible. The number of active site was not proportional to the reducibility because during the reduction, larger metal oxide particles were converted into larger metal particles. On the other hand, the number of active sites was inversely proportional to the particle sizes. The number of active site increased in the order M/Ahy < M/Aco < M/Aca. The catalytic activity also increased in the following order M/Ahy < M/Aco < M/Aca. The activity per active site increased according to the order M/Aca < M/Aco < M/Ahy meaning that for M/Ahy, a little increase in active site will lead to a significance increase in catalytic activity. It showed that Ahy has potential for the better support.
- OSTI ID:
- 22488957
- Journal Information:
- AIP Conference Proceedings, Vol. 1677, Issue 1; Conference: 5. international conference on mathematics and natural sciences, Bandung (Indonesia), 2-3 Nov 2014; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Design, Synthesis, and Mechanistic Evaluation of Iron-Based Catalysis for Synthesis Gas Conversion to Fuels and Chemicals
Technology development for cobalt F-T catalysts. Quarterly technical progress report No. 6, January 1, 1994--March 31, 1994