Synthesis and characterization of La{sub 0.6}Sr{sub 0.4}Fe{sub 0.8}Cu{sub 0.2}O{sub 3−δ} oxide as cathode for Intermediate Temperature Solid Oxide Fuel Cells
- Laboratorio de Cristalografía, Estado Sólido y Materiales, DETEMA, Facultad de Química, UdelaR, Gral. Flores 2124, Montevideo (Uruguay)
- Grupo Caracterización de Materiales, CAB-CNEA, Bustillo 9500, 8400 Bariloche (Argentina)
- Laboratorio de Fisicoquímica de Superficies, DETEMA, Facultad de Química, UdelaR, Gral. Flores 2124, Montevideo (Uruguay)
Nanocrystalline La{sub 0.6}Sr{sub 0.4}Fe{sub 0.8}Cu{sub 0.2}O{sub 3−δ} (LSFCu) material was synthetized by combustion method using EDTA as fuel/chelating agent and NH{sub 4}NO{sub 3} as combustion promoter. Structural characterization using thermodiffraction data allowed to determine a reversible phase transition at 425 °C from a low temperature R-3c phase to a high temperature Pm-3m phase and to calculate the thermal expansion coefficient (TEC) of both phases. Important characteristics for cathode application as electronic conductivity and chemical compatibility with Ce{sub 0.9}Gd{sub 0.1}O{sub 2−δ} (CGO) electrolyte were evaluated. LSFCu presented a p-type conductor behavior with maximum conductivity of 135 S cm{sup −1} at 275 °C and showed a good stability with CGO electrolyte at high temperatures. This work confirmed that as prepared LSFCu has excellent microstructural characteristics and an electrical conductivity between 100 and 60 S cm{sup −1} in the 500–700 °C range which is sufficiently high to work as intermediate temperature Solid Oxide Fuel Cells (IT-SOFCs) cathode. However a change in the thermal expansion coefficient consistent with a small oxygen loss process may affect the electrode-electrolyte interface during fabrication and operation of a SOFC. - Graphical abstract: Nanocrystalline La{sub 0.6}Sr{sub 0.4}Fe{sub 0.8}Cu{sub 0.2}O{sub 3−δ} was prepared by gel combustion and characterized by X-ray thermodiffraction and its conductivity was determined. The phase shows a reversible rhombohedral to cubic structural phase transition at 425 °C and a semiconductor to metallic phase transition at 275 °C. - Highlights: • LSFCu was prepared by gel combustion route using EDTA and NH{sub 4}NO{sub 3}. • LSFCu shows a reversible phase transition at 425 °C from R-3c to Pm-3m phase. • The sample has a maximum conductivity value of 135 S cm{sup −1} at 275 °C. • LSFCu shows a good chemical compatibility with CGO at 900 °C.
- OSTI ID:
- 22486738
- Journal Information:
- Journal of Solid State Chemistry, Vol. 228; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Synthesis, thermal expansion and high-temperature electrical conductivity of Co-doped (Y,Ca)FeO{sub 3−δ} with orthorhombic perovskite structure
Influence of Microstructure and Surface Activation of Dual-Phase Membrane Ce 0.8 Gd 0.2 O 2-δ -FeCo 2 O 4 on Oxygen Permeation
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
AMMONIUM NITRATES
CATHODES
CRYSTALS
CUPRATES
EDTA
ELECTRIC CONDUCTIVITY
INTERFACES
IRON COMPOUNDS
LANTHANUM COMPOUNDS
MICROSTRUCTURE
NANOSTRUCTURES
PEROVSKITE
PHASE TRANSFORMATIONS
P-TYPE CONDUCTORS
SOLID OXIDE FUEL CELLS
STRONTIUM COMPOUNDS
SYNTHESIS
THERMAL EXPANSION
TRIGONAL LATTICES